Abstract
The effect of finger joint location and distance from joint to joint one another on 3 point mid-concentration bending strength properties was investigated in this experiment. Resorcinol-phenol formaldehyde (RPF) and aqueous vinyl urethane (AVU) was used to domestic Pinus densiflora Sieb. et Zucc and imported Picea sitchensis Carr. that have been cut to different width of 0.15 mm between finger tip and root width and the distance from loading point to finger joint was 0, 30, 40, 50, 60 mm. The effect was not found on the location and distance of finger joint for bending modulus of elasticity, while the efficiency of bending strength property increased proportionally as the location of finger joint from the load point and the distance between finger joint increased. No influence was shown by finger joint location and distance beyond 3 times of specimen thickness, since similar values were shown between the solid wood and no destruction occurred materials.
소나무와 스프루스재를 사용하여 핑거공차를 0.15 mm로 고정하고 핑거피치 4.4 mm (Type S)와 6.8 mm(Type L)의 2종류 및 레조시놀 페놀 수지 접착제 및 수용성 비닐 우레탄 수지접착제로 2종류의 사용하여 종접합시키고 또한 2본의 종접합재를 이용하여 횡방향으로 핑거접합부를 양쪽으로 이동시키면서 접착하여 핑거접합부위의 배치거리를 접합재의 두께를 기준으로 하중점 중앙으로부터 양쪽 핑거접합부까지의 거리를 접합재 두께의 비율($R_t$) 0, 1.5, 2, 2.5, 3배의 5조건으로 제조하여 3점 중앙집중식 휨강도성능시험을 한 결과는 다음과 같다. 1) 휨탄성계수는 핑거접합부의 위치 이동과 관계없이 접착제의 종류, 핑거의 형상에 따른 영향은 나타나지 않았다. 2) 휨강도는 접착제의 종류, 핑거의 형상에 관계없이 하중점 중앙에서부터 멀어질수록 거의 직선적으로 증가하였으며 핑거접합부가 소재두께 비율의 3배에서는 소재와 같은 값을 나타내었다. 3) 시험편의 파괴는 하중점 중앙에서부터의 핑거접합부까지의 거리가 두께의 비율이 0, 1.5배에서 모두 핑거접합부에서 파괴되었으며 거리가 멀어질수록 접합부에서의 파괴가 적게 일어나다가 두께비율의 3배에서는 전혀 나타나지 않았다.