Abstract
In this study, NIMAX material has been processed using the three-dimensional measuring instrument and white light interferometer. they were tested to roundness and surface roughness and results are as follows: As for a cutting characteristic, it indicated that F4 showed a lower result than 2F showed due to the high hardness of the material and showed a good result when spindle rotation speed and tool feed were low. As for the measurement of roundness through 3-Dimensional measuring machine, it indicated that 4F showed a good result like the condition of cutting component and that roundness showed a good result when spindle rotation speed of 1,700 rpm and tool feed speed of 85 mm/min were applied. As for the surface roughness of processing surface, Surface roughness showed better 4F than 2F and conditions of spindle rotation speed 1,700 rpm, tool feed rate 55 mm/min showed good results in the Ra $0.4025{\mu}m$.
본 실험에서는 NIMAX재료를 3차원 측정기 및 백색광간섭계를 이용, 진원도 측정과 표면조도 측정을 하여 다음과 같은 결과를 얻었다. 절삭특성은 재료의 경도가 큰 관계로 2F의 조건보다 4F의 조건에서 낮게 나타났으며, 주축 회전수 및 공구 이송이 낮을수록 양호하게 나타났다. 3차원 측정기를 통한 진원도 측정은 절삭분력과 같은 4F 조건에서 양호하게 나타났으며, 주축회전수 1,700 rpm, 공구이송속도 85 mm/min의 조건에서 진원도는 양호한 결과를 보였다. 가공면의 표면거칠기는 2F 조건보다 4F의 조건에서 양호하게 나타났으며, 주축회전수 1,700 rpm, 공구이송속도 55 mm/min의 조건에서 Ra $0.4025{\mu}m$값을 보였다.