Abstract
Due to the recent shortage of well-graded river sand resulting from a rapid growth of concrete construction, sea sand, crushed sand, and etc. are increasingly used instead. It is, however, well noted that non-washed sea sand leads to corrosion of the reinforcing steel in concrete, and thus eventually results in damage to concrete. Also, the crushed sand is not being widely used, since it is difficult to maintain the allowable amount of passing 0.08mm sieve and to adjust grading. On the other hand, because the fine sand of Nakdong-River has a poor grading but good quality as a fine aggregate for concrete, it is strongly needed to investigate the fine sand as an alternative fine aggregate. Thus, the purpose of this research is to evaluate the physical properties of the fine sand of Nakdong-River to utilize it actively as a fine aggregate. For this purpose, after the sand samples were collected according to typical location of main stream of Nakdong-River, the physical properties such as density in oven-dry condition, grading, unit volume mass, and etc. of them were estimated. It was observed from the test results that physical properties of the fine sand of Nakdong-River except grading were found to be excellent.
최근, 건설공사의 급증으로 인한 양질의 하천모래의 고갈로, 콘크리트용 대체골재로서 바다모래, 부순모래 및 순환잔골재 등의 사용이 증가하고 있다. 그러나, 미세척 바다모래는 함유된 염화물로 인하여 철근콘크리트 구조물에 사용할 경우, 철근부식 유발로 구조물의 내구성에 악영향을 미치고, 부순모래는 미립분이 많고 입도조정이 어려워서 철근콘크리트 구조물에 널리 사용되지 못하고 있는 실정이다. 한편, 낙동강 세사는 낙동강 중 하류에 대규모로 분포하고 있고, 입도를 제외하면 콘크리트용 잔골재로서 품질이 우수하므로 이에 관한 연구가 시급히 요구되고 있다. 따라서 본 연구의 목적은 콘크리트 잔골재로서 낙동강 세사를 적극적으로 활용하기 위하여 그것의 물성을 평가하는 것이다. 이를 위하여 낙동강 본류 대표위치별로 시료를 채취하여 이들의 절건밀도, 입도, 단위용적질량 등의 물성을 평가하였는데, 그 결과 낙동강 세사는 입도를 제외하면 잔골재로서의 물성이 우수한 것으로 나타났다.