Abstract
Couple of laboratory for controlled low strength materials with bottom ash and recycled in-situ soil have been carried out. The optimum mix ratios for 4 cases with flowability and unconfined compressive strength were determined. The optimim mixing ratios were 25 to 45% of insitu soil, 30% of bottom ash, 10 to 20% of fly ash, 0 to 3% of crumb rubber, 3% of cement and 22% of water. Each mixture was satisfied the standard specification, minimum 20cm of flowability and 127 kPa of unconfined compressive strength. Two different curling methods, at room temperature and wet condition, were adopted. The average secant modulus(E50) was 0.07 to 0.08 * $q_u$. The compressive strength at wet condition showed 10% larger than at room temperature. The range of internal friction angle and cohesion for mixtures were 36.5o to 46.6o and 49.1 to 180 kPa, respectively. The mixture with crumb rubber(case 4) showed higher choesion and lower internal friction angle than the others. The pH of all the mixtures was over 12 which is strong alkine.
바톰애시와 현장발생토사를 혼합한 유동성뒤채움재에 실험적 연구를 수행하였다. 유동성과 일축압축강도를 이용하여 4가지 다른 배합조건에 대한 각각의 최적배합비를 결정하였다. 현장발생토 25-45%, 바톰애시 30%, 플라이애쉬 10-20%, 고무분말 0-3%, 시멘트 3% 및 물 22%의 범위에서 최적배합비가 결정되었다. 각각의 혼합물은 20cm 이상의 유동성, 3일 양생시 127 kPa 및 28일 양생시 206-980 kPa 일축압축강도 조건을 만족하였다. 시험재료는 상온양생 및 습윤양생 2가지 조건을 이용하였다. 전체 혼합물에 대한 변형계수(E50)는 0.07-0.08 * $q_u$로 나타났다. 또한, 습윤양생 시편의 일축압축강도가 상온양생 시편에 비해 약 10% 정도 큰 값을 나타나내었다. 전체혼합물의 내부마찰각은 36.5-46.6도, 점착력은 49.1-180 kPa 범위로 측정되었다. 고무분말이 추가된 case 4번의 경우 다른 case에 비해 점착력은 크게, 내부마찰각은 작은 값을 나타내었다. 유동성채움재의 공용 성능을 위해 실시한 pH실험 결과 배합초기 12이상 강알칼리성으로 평가되었다.