A Scientific Analysis on the Glass Beads Excavated from the Daho-ri site NO. 6, Changwoen

창원 다호리 유적 6호분 출토 유리구슬의 과학적 분석

A scientific analysis was carried out on the 14 pieces of glass beads excavated from the Daho-ri site NO. 6, Changweon. Most of the glass pieces were made of light blue transparent glass with round bubbles aligned in a regular direction. As a result of the SEM-EDS analysis, all the glass pieces turned out to be within the potash glass group (K₂O-SiO₂) and were identified to be the LCA (Low CaO, Low Al₂O₃) series glass, of which the concentration is 5% or below for CaO and Al₂O₃ respectively. In addition, it is presumed that plant materials were refined or a mineral (saltpetre, KNO₃) was used as the raw materials for making potash and also that the ingredient acting as a colorants for light blue color was affected deeply by CuO.

창원 다호리 유적 6호분에서 출토된 유리구슬편 14점에 대하여 과학적인 분석을 실시하였다. 유리편은 대부분 감청색의 투명한 유리로 원형의 기포들이 일정한 방향으로 나열되어 있다. SEM/EDS 분석결과 유리편은 모두 포타쉬유리군(K₂O-SiO₂)이며 CaO 및 Al₂O₃의 함량은 모두 5%이하인 LCA(Low CaO, Low Al₂O₃)계 유리로 확인되었다. 또한 포타쉬원료는 식물제를 정제하거나 광물(초석, KNO₃)을 사용한 것으로 판단되며 감청색을 내는 발색제로 작용하는 성분은 CuO의 영향이 큰 것으로 판단된다.