Abstract
SCM420 steel tempered after performing gear hove PACVD carbide coating on the surface after the cutting surface hardness was high. Difficult-to-cut, without coating is classified as mild as large, including materials like mild, high strength that improves tool life and productivity have limited availability. Drive to improve it in the TiCN-coated carbide call for war to the finish coating on cutting a hob skiving good workability, tool wear less, 2.5-fold increase in tool life results were obtained. Experiments using CNC Skiving hobbing machine with wet cutting conditions, cutting speed and feed rate to apply a variety of the tool wear and surface roughness data were obtained. Results from condition 2 (V = 200m/min F = 0.7mm/rev) cutting speed feed mark the cutting surface microstructure and surface roughness Rmax $4.7{\mu}m$(Ra $1.19{\mu}m$) of the data was obtained.
SCM420재질의 기어를 담금질을 실시한 후 초경호브(Hob)에 PACVD 코팅처리 후 표면경도가 높은 표면(HRC 60)을 절삭하였다. 코팅처리 없이 난삭재(難削材)로 분류되는 경도가 큰것, 경한 물질을 포함한 것, 강도가 높은 것에 공구수명과 생산성을 향상에는 한계성을 가지고 있다. 이를 개선하기 위해 초경호브에 TiCN코팅처리 전후에 대하여 Skiving 절삭으로 코팅처리 한 호브가 가공성이 좋고, 공구마멸이 적어, 공구수명이 2.5배 증가하는 결과를 얻었다. 실험은 CNC 스카이빙 호빙머신을 이용하여 습식절삭으로 절삭속도와 이송량으로 다양한 조건을 적용하여 공구마멸과 표면거칠기 데이터를 얻었다. 실험결과 조건 2에서(V=200m/min F=0.7mm/rev) Cutting speed가 절삭표면에 Feed Mark가 미세하고, 표면거칠기는 Rmax $4.7{\mu}m$(Ra $1.19{\mu}m$)의 데이터를 얻었다.