Study on the Properties of Flexible Polyurethane Foam at the Aging Condition

연질 폴리우레탄 폼의 노화 특성 연구

  • Kim, Chang-Bum (Department of Chemical Engineering, Kyonggi University) ;
  • Kim, Sangbum (Department of Chemical Engineering, Kyonggi University)
  • Received : 2012.12.07
  • Accepted : 2012.12.28
  • Published : 2012.12.31
Download PDF
⟨ Previous Next ⟩

Abstract

In order to establish the cause of the deformation of polyurethane foam, compression set was measured according to the aging temperature and time. FT-IR, TGA, DSC and DMA were used for investigating the cause of deformation of aged PUF. The results of FT-IR and TGA reveals that no structure change occurred during deformation of PUF. Resilience of aged PUF was reduced by the increase of reduction ratio in storage modulus over the glass transition temperature of hard segment.

본 연구에서는 폴리우레탄 폼의 변형이 발생하는 원인을 규명하기위해 합성된 폴리우레탄 폼을 온도와 노화시간을 다르게 하여 영구압축음율을 측정하였다. 폼의 변형의 원인을 알아보기 위해 FT-IR로 구조분석을 하였으며 TGA, DSC, DMA를 통해 열분석을 진행 하였다. 실험 결과 폼의 변형이 발생하기 위해서는 일정량 이상의 열에너지가 필요하다는 것을 알았으며 FT-IR 결과 폼의 변형이 발생으로 인한 구조의 변화가 발생하지 않는다는 것을 확인하였다. 열분석 결과 폼의 변형이 발생하는 온도 구간에서 분해에 의한 무게 감소가 없었으며 열 흐름상에는 특별한 차이가 없었다. 그러나 hard segment의 유리전이온도 이상부터 저장 모듈러스 감소율이 커졌으며 이로 인해 복원력이 감소한 것을 알았다.

Keywords

References

  1. G. Woods, The ICI polyurethane book 2nd ed., John Wiley & Sons, New York (1990)
  2. J. P. Armistead, G. L. Wilkes, and R. B. Turner, J. Appl. Polym. Sci., 35, 601 (1988) https://doi.org/10.1002/app.1988.070350305
  3. O. Olabisi, L. M. Robeson, M. T. Shaw, Polymer -polymer miscibility, 1st ed., Academic Press, New York (1979)
  4. E. Tocha, H. Janik, M. Debowski, G. J. Vancso, J. Macromol. Sci. Phys., 41, 1291 (2002) https://doi.org/10.1081/MB-120013098
  5. A. L. Chang, R. M. Briber, E. L. Thomas, R. J. Zdrahala, and F. E. Critchfield, Polymer, 23, 1060 (1982) https://doi.org/10.1016/0032-3861(82)90409-8
  6. H. Nishimura, H. Kojima, T. Yarita, and M. Noshiro, Polym. Eng. Sci., 26, 585 (1986) https://doi.org/10.1002/pen.760260902
  7. M. F. Sonnenschein, R. Prange, A. K. Schrock, Polymer, 48, 616 (2007) https://doi.org/10.1016/j.polymer.2006.11.021
  8. J. M. Van der Schuur, E. E. Van der Heide, J. Feijen, R. J. Gaymans Polymer, 46, 3616 (2005) https://doi.org/10.1016/j.polymer.2005.03.010
  9. J. M. Van der Schuur, E. van der Heide, J. Feijen, R. J. Gaymans, Polymer, 45, 2721 (2004) https://doi.org/10.1016/j.polymer.2004.02.016
  10. R. Neff, C. W. Macosko, A. J. Ryan, J. Appl. Polym. Sci. : Polym. Phys., 36, 573 (1998)
  11. M. F. Sonnenschein, B. L. Wendt, A. K. Schrock, J. M. Sonney, A. J. Ryan, Polymer, 49, 934 (2008) https://doi.org/10.1016/j.polymer.2008.01.008
  12. C. H. Smith, S. L. Degisi, J. Appl. Polym. Sci., 10, 795 (1966) https://doi.org/10.1002/app.1966.070100512
  13. J. T. Koberstein, A. F. Galambos, L. M. Leung, Macromolecules, 25, 6195 (1992) https://doi.org/10.1021/ma00049a017
  14. J. C. Moreland, G. L. Wilkes, R. B. Turner, J. Appl. Polym. Sci., 52, 549 (1994) https://doi.org/10.1002/app.1994.070520411

Cited by

  1. 인공 화재 실험을 통한 광해방지 응급조치용 우레탄 폼 재료 특성 및 적정 복토에 관한 연구 vol.53, pp.3, 2012, https://doi.org/10.9719/eeg.2020.53.3.287
  2. 교반기의 임펠러 형태에 따른 폴리우레탄 폼의 미세구조와 물성 연구 vol.34, pp.1, 2012, https://doi.org/10.7234/composres.2021.34.1.016