The study attempted to find out any effect to prevent photo aging of epoxy resin used for conservation by way of adding UV stabilizer, one of plastic additives. Specimens were made by adding HALS and UVA UV stabilizer as each concentration to 3 kinds of epoxy resin, which are most frequently used for artifacts joining and restoration process, and aging effects were investigated through Color change, SEM, contact angle, FTIR analysis during UV aging experiments. Last, usage suitability was checked when UV stabilizer was added through Universal Tensile strength tester. In result, it is impossible to prevent decomposition of chemical structure in spite of adding UV stabilizer but in the case of epoxy A and R, it is believed that photo aging such as yellowing or crack can be minimized without giving a big influence to adhesive strength of epoxy resin through adding less than 0.1% of UVA. It is expected that above will solve photo aging problem of epoxy resin used for joining and restoration of artifacts and will extend its life as joining and restoration materials.
문화재 보존처리 시 사용되는 에폭시계수지에 플라스틱 첨가제 중 하나인 자외선 안정제를 첨가함으로써 수지의 광노화를 예방하는데 효과가 있는지 알아보고자 하였다. 문화재 접합 및 복원 과정에서 많이 사용되는 3가지 에폭시계수지에 HALS계와 UVA계 자외선 안정제를 농도별로 첨가하여 시편을 제작하였으며, 자외선 노화 실험을 실시하여 색도 변화, SEM 관찰, 접촉각, FT-IR 분석을 하였다. 또한 인장 전단 접착 강도 시험을 통해 자외선 안정제 첨가 유무에 따른 에폭시계수지의 물성 변화를 확인하였다. 분석 결과, 자외선 안정제를 첨가하여도 화학 구조상의 분해를 방지할 수 없지만 에폭시 R과 에폭시 A는 UVA계 자외선 안정제를 0.1% 이하 첨가함으로써 에폭시계수지의 접착 강도에 크게 영향을 미치지 않고 황변현상이나 균열과 같은 광노화로부터 최소화 할 수 있음을 확인하였다. 이를 통해 문화재접합 및 복원에 사용되는 에폭시계수지의 광노화 문제점을 보완하고 접합 및 복원재로서의 수명을 연장시킬 수 있을 것으로 기대된다.