Curing efficiency of various resin-based materials polymerized through different ceramic thicknesses and curing time

  • Lee, Jung-Won (Department of Dentistry, College of Medicine, University of Ulsan) ;
  • Cha, Hyun-Suk (Department of Dentistry, College of Medicine, University of Ulsan) ;
  • Lee, Joo-Hee (Department of Dentistry, College of Medicine, University of Ulsan)
  • 투고 : 2011.04.25
  • 심사 : 2011.06.07
  • 발행 : 2011.09.30

초록

PURPOSE. The aim of this in vitro study was to examine the curing efficiency of various resin-based materials polymerized through ceramic restorations with 3 different thicknesses. Curing efficiency was evaluated by determining the surface microhardness (VHN) of the resin specimens. MATERIALS AND METHODS. Four kinds of resin materials were used. Z350 (3M ESPE $Filtek^{TM}$ Z350: A2 Shade), Z250 (3M ESPE $Filtek^{TM}$ Z250: A2 Shade) and $Variolink^{(R)}$ II (VL: Ivoclar vivadent, base: transparent) either with or without a self-curing catalyst (VLC: Ivoclar vivadent, catalyst: low viscosity/transparent) were filled into the silicone mold (10 mm diameter, 1 mm thick). They were cured through ceramic discs (IPS e.max Press MO-0 ingot ivoclar vivadent, 10 mm diameter, 0.5, 1 and 2 mm thicknesses) by LED light-curing units for 20 and 40 seconds. Vicker's microhardness numbers (VHNs) were measured on the bottom surfaces by a microhardness tester. Data were analyzed using a 3-way analysis of variance (ANOVA) at a significance level of 0.05. RESULTS. The thickness of ceramic disc increased, the VHNs of all four resin types were decreased (P<.05). The mean VHN values of the resins light cured for 40 seconds were significantly higher than that of LED for 20 seconds in all four resin materials (P<.05). VLC showed significantly higher VHN values than VL regardless of other conditions (P<.05). Z350 and Z250 showed higher values than VL or VLC (P<.01). CONCLUSION. Thinner ceramic disc with increased curing time resulted higher VHN values of all resin materials. The use of a catalyst produced a greater hardness with all polymerization methods. Restorative resin materials (Z350, Z250) showed higher VHN values than resin cement materials (VL, VLC).

키워드

참고문헌

  1. Asmussen E. Restorative resins: hardness and strength vs. quantity of remaining double bonds. Scand J Dent Res 1982; 90:484-9.
  2. Caughman WF, Caughman GB, Shiflett RA, Rueggeberg F, Schuster GS. Correlation of cytotoxicity, filler loading and curing time of dental composites. Biomaterials 1991;12:737-40. https://doi.org/10.1016/0142-9612(91)90022-3
  3. El-Mowafy OM, Rubo MH. Influence of composite inlay/onlay thickness on hardening of dual-cured resin cements. J Can Dent Assoc 2000;66:147.
  4. Cheong C, King NM, Pashley DH, Ferrari M, Toledano M, Tay FR. Incompatibility of self-etch adhesives with chemical/dualcured composites: two-step vs one-step systems. Oper Dent 2003;28:747-55.
  5. Suh BI, Feng L, Pashley DH, Tay FR. Factors contributing to the incompatibility between simplified-step adhesives and chemically- cured or dual-cured composites. Part III. Effect of acidic resin monomers. J Adhes Dent 2003;5:267-82.
  6. Calamia JR, Calamia CS. Porcelain laminate veneers: reasons for 25 years of success. Dent Clin North Am 2007;51:399-417. https://doi.org/10.1016/j.cden.2007.03.008
  7. Garber DA, Goldstein RE. Porcelain and composite inlays and onlays: esthetic posterior restorations. Chicago; Quintessence Publishing Co.; 1994.
  8. Strang R, Macdonald I, O'Hagan S, Murray J, Stephen KW. Variations in performance of curing light units by determination of composite resin setting time. Br Dent J 1987;162:63-5. https://doi.org/10.1038/sj.bdj.4806026
  9. Blackman R, Barghi N, Duke E. Influence of ceramic thickness on the polymerization of light-cured resin cement. J Prosthet Dent 1990;63:295-300. https://doi.org/10.1016/0022-3913(90)90199-M
  10. Peutzfeldt A, Asmussen E. The effect of postcuring on quantity of remaining double bonds, mechanical properties, and in vitro wear of two resin composites. J Dent 2000;28:447-52. https://doi.org/10.1016/S0300-5712(00)00021-X
  11. Pianelli C, Devaux J, Bebelman S, Leloup G. The micro- Raman spectroscopy, a useful tool to determine the degree of conversion of light-activated composite resins. J Biomed Mater Res 1999;48:675-81. https://doi.org/10.1002/(SICI)1097-4636(1999)48:5<675::AID-JBM11>3.0.CO;2-P
  12. Shortall AC, Harrington E. Effect of light intensity on polymerisation of three composite resins. Eur J Prosthodont Restor Dent 1996;4:71-6.
  13. Koch A, Kroeger M, Hartung M, Manetsberger I, Hiller KA, Schmalz G, Friedl KH. Influence of ceramic translucency on curing efficacy of different light-curing units. J Adhes Dent 2007;9:449-62.
  14. Hooshmand T, Mahmoodi N, Keshvad A. Microhardness of a resin cement polymerized by light-emitting diode and halogen lights through ceramic. J Prosthodont 2009;18:411-6. https://doi.org/10.1111/j.1532-849X.2009.00449.x
  15. Hofmann N, Papsthart G, Hugo B, Klaiber B. Comparison of photo- activation versus chemical or dual-curing of resin-based luting cements regarding flexural strength, modulus and surface hardness. J Oral Rehabil 2001;28:1022-8. https://doi.org/10.1046/j.1365-2842.2001.00809.x
  16. Rueggeberg FA, Craig RG. Correlation of parameters used to estimate monomer conversion in a light-cured composite. J Dent Res 1988;67:932-7. https://doi.org/10.1177/00220345880670060801
  17. Rueggeberg FA, Ergle JW, Mettenburg DJ. Polymerization depths of contemporary light-curing units using microhardness. J Esthet Dent 2000;12:340-9. https://doi.org/10.1111/j.1708-8240.2000.tb00243.x
  18. Magne P, Belser U. Bonded porcelain restorations in the anterior dentition-a biomimetic approach. Chicago: Quintessence Publishing Co., 2002.
  19. Jung H, Friedl KH, Hiller KA, Haller A, Schmalz G. Curing efficiency of different polymerization methods through ceramic restorations. Clin Oral Investig 2001;5:156-61. https://doi.org/10.1007/s007840100118
  20. Rasetto FH, Driscoll CF, von Fraunhofer JA. Effect of light source and time on the polymerization of resin cement through ceramic veneers. J Prosthodont 2001;10:133-9. https://doi.org/10.1111/j.1532-849X.2001.00133.x
  21. Santos GC Jr, El-Mowafy O, Rubo JH, Santos MJ. Hardening of dual-cure resin cements and a resin composite restorative cured with QTH and LED curing units. J Can Dent Assoc 2004;70: 323-8.
  22. Moon HJ, Lee YK, Lim BS, Kim CW. Effects of various light curing methods on the leachability of uncured substances and hardness of a composite resin. J Oral Rehabil 2004;31:258-64. https://doi.org/10.1111/j.1365-2842.2004.01172.x
  23. O'Keefe KL, Pease PL, Herrin HK. Variables affecting the spectral transmittance of light through porcelain veneer samples. J Prosthet Dent 1991;66:434-8. https://doi.org/10.1016/0022-3913(91)90501-M
  24. Brodbelt RH, O'Brien WJ, Fan PL. Translucency of dental porcelains. J Dent Res 1980;59:70-5. https://doi.org/10.1177/00220345800590011101
  25. Akgungor G, Akkayan B, Gaucher H. Influence of ceramic thickness and polymerization mode of a resin luting agent on early bond strength and durability with a lithium disilicate-based ceramic system. J Prosthet Dent 2005;94:234-41. https://doi.org/10.1016/j.prosdent.2005.04.020
  26. Rueggeberg FA, Caughman WF. The influence of light exposure on polymerization of dual-cure resin cements. Oper Dent 1993;18:48-55.
  27. van Meerbeek B, Inokoshi S, Davidson CL, De Gee AJ, Lambrechts P, Braem M, Vanherle G. Dual cure luting composites- Part II: Clinically related properties. J Oral Rehabil 1994;21:57-66. https://doi.org/10.1111/j.1365-2842.1994.tb01124.x

피인용 문헌

  1. Avaliação da influência da solução de irrigação na resistência adesiva de um cimento resinoso vol.42, pp.2, 2013, https://doi.org/10.1590/S1807-25772013000200003
  2. Effect of Ceramic Thickness and Shade on Mechanical Properties of a Resin Luting Agent vol.23, pp.6, 2014, https://doi.org/10.1111/jopr.12140
  3. Efficiency of Dual-Cured Resin Cement Polymerization Induced by High-Intensity LED Curing Units Through Ceramic Material vol.40, pp.2, 2015, https://doi.org/10.2341/13-357-L
  4. Efeito da intensidade de fontes de luz e barreiras de cerâmica na microdureza de cimento resinoso dual vol.44, pp.4, 2015, https://doi.org/10.1590/1807-2577.1083
  5. Polymerization Efficiency of a Dual-Cured Resin Cement through Zirconia with Three Different Cusp Inclinations vol.2018, pp.2314-4939, 2018, https://doi.org/10.1155/2018/8684245
  6. Polymerization efficiency of two dual-cure cements through dental ceramics vol.49, pp.1, 2011, https://doi.org/10.17096/jiufd.25575
  7. Effect of Different Thicknesses of Pressable Ceramic Veneers on Polymerization of Light-cured and Dual-cured Resin Cements vol.16, pp.5, 2011, https://doi.org/10.5005/jp-journals-10024-1688
  8. Water Sorption and Solubility of Luting Agents Used Under Ceramic Laminates With Different Degrees of Translucency vol.41, pp.5, 2011, https://doi.org/10.2341/15-201-l
  9. Influence of material thickness on fractural strength of CAD/CAM fabricated ceramic crowns vol.36, pp.6, 2011, https://doi.org/10.4012/dmj.2016-296
  10. The Effect of Ceramic Thickness on the Surface Microhardness of Dual-cured and Light-cured Resin Cements vol.20, pp.4, 2011, https://doi.org/10.5005/jp-journals-10024-2540
  11. Study of physicochemical properties and effects on bonding to zirconia ceramics of five resin cements vol.34, pp.18, 2011, https://doi.org/10.1080/01694243.2020.1749449
  12. Effect of Light-Sources and Thicknesses of Composite Onlays on Micro-Hardness of Luting Composites vol.14, pp.22, 2011, https://doi.org/10.3390/ma14226849