PP/talc 컴파운드의 talc 분산성 및 유변학적 특성 연구

  • You, Young-Chul (Polymer Science & Engineering, Kongju National University) ;
  • Kim, Youn-Cheol (Polymer Science & Engineering, Kongju National University)
  • 유영철 (공주대학교 신소재공학부 고분자공학) ;
  • 김연철 (공주대학교 신소재공학부 고분자공학)
  • Received : 2011.08.03
  • Accepted : 2011.09.08
  • Published : 2011.09.30

Abstract

Polypropylene (PP)/talc compounds with talc content of 20wt% were fabricated by master-batch (MB) and direct compounding method using injection molding. The MB was prepared by mini compounder at $200^{\circ}C$ and the content of talc was 50wt%. The talc dispersion of the PP/talc compound was investigated by SEM-EDS. The talc was well dispersed within PP matrix in case of the MB-PP compound using MB. The rheological properties of the PP/talc compounds were measured by dynamic Rheometer. The MB-PP compound indicates higher shear thinning and elastic property than direct compound. The disperion of talc was certified by G'-G" plot, and Van Gurp-Palmen analysis was applied in order to certify an increase in elasticity.

폴리프로필렌(polypropylene, PP)/talc 컴파운드를 talc의 조성을 20wt%로 하여 마스터뱃취(master-batch, MB)와 사출기를 이용한 직접 제조법으로 각각 제조하였다. MB는 talc 함량을 50wt%로 하여 소형 혼합기(mini compounder)로 $200^{\circ}C$에서 제조하였다. SEM-EDS를 이용하여 PP/talc 컴파운드의 talc 분산정도를 평가하였다. MB를 이용하여 제조한 컴파운드의 talc 분산성이 우수하게 나타났다. PP/talc 컴파운드의 유변학적 특성을 동적유변측정기를 이용하여 측정하였다. MB를 이용한 MB-PP 컴파운드가 직접 제조한 컴파운드보다 shear thinning과 탄성특성이 증가하였다. G'-G" plot의 기울기 변화로부터 talc 분산성 정도를 확인하였고, 탄성특성 증가를 확인하기 위해 Van Gurp-Palmen 분석을 이용하였다.

Keywords

References

  1. M.i Fujiyama and T. Wakino, "Crystal orientation in injection molding of talc-filled polypropylene", J. of Appl. Polym. Sci., 42, 9-20, 1991. https://doi.org/10.1002/app.1991.070420103
  2. J. I. Velasco, J. A. De Saja, and A. B. Martínez1, "Fracture behavior of untreated and silane-treated talc-filled polypropylene composites", Fatigue & Fracture of Eng. Mat. & Structures, 20, 659-670, 1997. https://doi.org/10.1111/j.1460-2695.1997.tb00299.x
  3. Y. Zhou and P. K. Mallick, "Effects of temperature and strain rate on the tensile behavior of unfilled and talc-filled polypropylene. Part I: Experiments", Polym. Eng. & Sci., 42, 2449-2460, 2002. https://doi.org/10.1002/pen.11131
  4. R. S. Hadal, A. Dasari2, and R. D. K. Misra, A "Microstructural study of sequence of events leading to fracture of wollastonite-reinforced polypropylene composites during tensile loading", Microscope and Microanalysis, 10, 670-671, 2004.
  5. Y. Zhou and P. K. Mallick, "Effects of melt temperature and hold pressure on the tensile and fatigue properties of an injection molded talc-filled polypropylene", Polym. Eng. & Sci., 45, 755-763, 2005. https://doi.org/10.1002/pen.20301
  6. K. Shelesh-Nezhad and A. Taghizadeh, "Shrinkage behavior and mechanical performances of injection molded polypropylene/talc composites", Polym. Eng. & Sci., 47,2124-2128, 2007. https://doi.org/10.1002/pen.20940
  7. H. Azizi and J. Faghihi, "An investigation on the mechanical and dynamic rheological properties of single and hybrid filler/polypropylene composites based on talc and calcium carbonate", Polym. Compo., 30, 1743-1748, 2009. https://doi.org/10.1002/pc.20685
  8. J. M. Cormont, "In line compounding and extrusion of PP with talc and chalk", Adv. in Polym. Techno., 5, 139-152, 1985. https://doi.org/10.1002/adv.1985.060050205
  9. D. C. Goel, "Effect of polymeric additives on the rheological properties of talc-filled polypropylene", Polym. Eng. & Sci., 20, 198-201, 1980. https://doi.org/10.1002/pen.760200305
  10. Y. C. Kim and J.-C. kim, "Study on the Silicate Dispersion and Rheological Properties of PP/Starch-MB/Silicate Composites", J. Ind. Eng. Chem., 13, 1029-1034, 2007.
  11. S. Duquesne1, F. Samyn1, S. Bourbigot, P. Amigouet, F. Jouffret, and K. Shen, "Influence of talc on the fire retardant properties of highly filled intumescent polypropylene composites", Polym. for Adv. Techno., 19, 620-627, 2008. https://doi.org/10.1002/pat.1127
  12. Y. Jahani and M. Ehsani, "The rheological modification of talc-filled polypropylene by epoxy-polyester hybrid resin and its effect on morphology, crystallinity, and mechanical properties", Polym. Eng. & Sci., 49, 619-629, 2009. https://doi.org/10.1002/pen.21294
  13. Y. Jahani, "Comparison of the effect of mica and talc and chemical coupling on the rheology, morphology, and mechanical properties of polypropylene composites", Polym. for Adv. Techno.., 22, 942-950, 2011. https://doi.org/10.1002/pat.1600
  14. C. D. Han, D. M. Baek, and J. G. Kim, "Effect of microdomain structure on the order-disorder transition temperature of polystyrene-block-polyisoprene-blockpolystyrene copolymers", Macromolecules, 23, 561-570, 1990. https://doi.org/10.1021/ma00204a032
  15. D. J. Lohse, S. T. Milner, L. J. Fetters, and Xenidou, "Well-Defined, Model Long Chain Branched Polyethylene. 2. Melt Rheological Behavior", Macromolecules, 35, 3066-3075 2002. https://doi.org/10.1021/ma0117559