Abstract
We successfully grew $La_{0.35}Pr_{0.35}Ca_{0.3}MnO_3$(LPCMO)/$LaAlO_3$(LAO) thin film using Laser Molecular-Beam Epitaxy and studied post-growth annealing effects ($750^{\circ}C$, 5 h) on its crystal structural and magnetic properties. Whereas the single-layered LPCMO and LPCMO/STO superlattice thin films show rough surface before and after the post-growth annealing, LPCMO/LAO superlattice shows a relatively very flat surface even after the post-growth annealing. The enhancement of ferromagnetism of LPCMO/LAO superlattice after the post-growth annealing was remarkable compared to the single-layered LPCMO thin film. The coercive and saturation magnetic field of the single-layed LPCMO thin film were decreased after the post-annealing. However, for LPCMO/LAO superlattice, a same coercive and increased saturation magnetic field were exhibited after post-growth annealing. We suggest that these peculiar observations are originate from the super-structure of LPCMO and LAO.
Laser Molecular-Beam Epitaxy 방법을 사용하여 $La_{0.35}Pr_{0.35}Ca_{0.3}MnO_3$(LPCMO)/$LaAlO_3$(LAO) 초격자를 성공적으로 증착하였으며 이의 열처리 전후 결정학적, 자기적 특성을 LPCMO 단층박막, 그리고 LPCMO/$SrTiO_3$(STO) 초격자와 비교 분석하였다. LPCMO 단층박막, 그리고 LPCMO/STO 초격자 단층박막의 경우, 표면이 열처리 전후 모두 거친 양상을 보인 것과는 달리 LPCMO/LAO 초격자 박막은 열처리 전후 모두 상대적으로 매우 매끈하였다. 열처리 후 단층박막, 초격자 박막 시료 모두 강자성 특성이 향상되었으며 특히 초격자의 경우에는 이러한 현상이 두드러졌다. 열처리 후에 보자력과 포화자기장이 감소하는 LPCMO 단층박막과는 달리 LPCMO/LAO 초격자의 경우, 열처리 후에도 보자력은 열처리 전과 같은 값을 보였으며 단층박막과는 반대로 포화자기장은 오히려 증가하였다. 이러한 자기적 특성은 절연체 사이에 강자성체가 끼여 있는 초격자라는 결정구조에서 기인하는 것으로 이해된다.