Abstract
Paved roads are suffered from the permanent plastic deformation in hot summer and cracks in cold winter, which are detrimental to safe driving. This leads to necessity of modification of asphalt to resist those deformation. In this study, two kinds of modifiers were examined; organic polymers and a photoinitiator which is activated by ultraviolet lay. The mechanical and rheololgical properties of modified asphalts were examined using UTM and rheometer. Results showed that the properties were varied depending on the types of polymer and irradiation time. UV irradiation increased the tensile strength and storage modulus of thermoplastic polymer-modified asphalt, however UV was not effective on thermoset polymer. According to long term ultraviolet curing test, properties of the polymer/photoinitiator-modified asphalt did not decrease, but rather increase for 20 years. This indicates that the useful life of the asphalt could be extended by addition of photoinitiator.
여름철 아스팔트의 표면 온도 상승으로 인한 도로의 소성변형과 겨울철 온도 강하로 인한 도로균열이 도로안전 운전을 위협하는 문제로 등장하면서 아스팔트 물성향상을 위한 아스팔트개질의 필요성이 대두되고 있다. 본 연구에서는 아스팔트의 탄성과 소성변형저항성을 증가시키기 위해 아스팔트 물성 노화의 직접적 원인인 햇빛, 특히 자외선을 이용하기 위해, 고분자중합에 사용되는 광개시제를 사용하여 고분자로 개질된 아스팔트를 다시 개질하였다. 인장시험기와 레오미터를 이용하여 기계적 물성과 유변학적 물성을 실험한 결과 열가소성고분자개질아스팔트는 자외선에 의한 가교반응으로 인해 인장강도와 저장탄성률이 크게 증가하였으나 열경화성고분자개질아스팔트에는 영향을 끼치지 못하였다. 장시간 자외선조사 시험에서는 조사시간이 길어짐에 따라 그 물성이 증가되거나 유지되는 거동을 보임으로써 자외선이 아스팔트의 사용수명이 20년이 될 수 있는 효과를 나타내었다.