Abstract
This paper presents the probabilistic analysis for fatigue life of Glass/Epoxy laminates with impact-induced damage. For this, a series of impact tests were perfomed on the Glass/Epoxy laminates using instrumented impact testing machine. Then, tensile and fatigue tests carried out so as to generate post-impact residual strength and fatigue life. Two Parameter Weibull distribution was used to fit the residual strength and fatigue life data of Glass/Epoxy composite laminates. The residual strength was affected by impact energy and their variance decreased with increasing of impact energy. The fatigue life of impacted laminates was greatly reduced by impact energy and this trend depended on applied stress amplitude. Additionally, the variation of fatigue life was gradually decreased with the applied stress amplitude.
본 논문에서는 충격손상 복합재료의 피로수명 저하 특성과 이의 변동성을 통계적으로 분석하였다. 충격손상 복합재료의 잔류강도는 2모수 Weibull 분포에 잘 적합되었으며 충격에너지의 증가에 따라 잔류강도의 변동성은 감소 하였다. 복합재료의 피로수명은 충격손상에 의하여 크게 저하되었으며 또한 이의 피로수명에 대한 충격손상의 영향은 작용 응력진폭에 따라 변화함을 알 수 있었다. 또한 2모수 Weibull 분포를 이용하여 충격손상 복합재료의 피로수명의 변동성을 추정하였으며 충격에너지의 증강 및 응력진폭의 감소에 따라 피로수명의 변동성은 점차 감소하였다.