Abstract
$Ni_3Al$ is known as a good high temperature structural material because of high yield strength at ambient temperature. However, it is too brittle to use as a structural material because of their weak grain boundary. In this work, orientation measurement and related mechanical properties of directionally solidified NiAl/$Ni_3Al$ two-phase alloys with various compositions (Ni-23~27 at.%Al) were investigated for developing multi-phase DS-processed alloys with the growth rates of 10, 50 and 100 ${\mu}m/s$ in a modified Bridgeman type furnace. It was found that the multi-phase microstructures such as the $\gamma$ dendrite +${\gamma}'$ matrix duplex microstructure was formed in the hypoeutectic composition of 23 at.%Al, $\beta$ dendrite +${\gamma}'$ matrix duplex microstructure in the hypereutectic composition of 26 and 27 at.%Al. And ${\gamma}'$ single phase was formed in the composition of 24.5 and 25 at.%Al. The hypoeutectic alloy including $\gamma$ dendrites with ${\gamma}'$ matrix showed a large elongation of over 70% at room temperature. However, the room-temperature tensile elongation decreased with increasing Al contents because the volume fraction of brittle $\beta$ dendrites in the ductile ${\gamma}'$ matrix increased.