Characterization of dissociation catalysts for waste plastics

폐플라스틱 분해 촉매의 특성

Catalytic dissociation reaction was studied in order to transform waste plastics to oil by using noble metal supported catalysts. XRD, SEM, and GC/MSD analysis were performed to find the crystalline structure and shape, and product distribution. Generally, dissociation reaction occurs at low temperature compared to pyrolysis. Dissociation reaction has advantage of gasoline yield with respect to pyrolysis which products mainly $C_1\simC_4$. The result of dissociation reaction, gasoline was obtained much as a product. $C_5\simC_{11}$ compounds were produced as a gasoline product on Pt-zeolite among noble metal catalysts at $340^{\circ}C$. The conversion of dissociation reaction of waste plastics on the prepared catalyst was above 70% over $340^{\circ}C$.

폐플라스틱을 오일로 전환하기 위하여 귀금속이 담지된 촉매를 사용하여 촉매 분해반응을 연구 하였다. 제조된 촉매의 결정 구조, 결정형태, 접촉분해 후 생성물의 분포를 알고자 XRD, SEM, GC/MSD 등의 분석을 시행하였다. 접촉분해 반응은 열분해반응에 비해서 저온에서 일어나며, 열분해생성물이 $C_1\simC_4$의 가스상이 대부분인데 비해, 액상화합물이 많아 휘발유 생성에 유리한 면이 있다. 접촉 분해반응결과 휘발유 성분이 많이 생성되었다. 귀금속이 담지된 촉매중 Pt-zeolite 촉매가 $340^{\circ}C$에서 $C_5\simC_{11}$ 근처의 휘발유 성상의 생성물 분포가 가장 많이 나타났으며, $340^{\circ}C$ 이상부터는 폐플라스틱(PE, PP, ABS)에 대해서 접촉 분해반응 전환율이 약 70% 이상인 것으로 나타났다.