Abstract
Very-early strength latex-modified concrete (VES-LMC) was developed for the purpose of fast-track overlay of a concrete bridge deck under heavy traffic, concentrated on the workability, durability, and strength gain so that it can be opened to the traffic only three hours after its placement. The mixture of VES-LMC might accompany very high heat of hydration at early-age because of its inherent rapid hardening property and could have susceptibility to autogenous shrinkage because of its relatively low water-cement ratio. This study evaluated the effect of the latex-cement ratio(L/C) both of the constant and variable slumps on the autogenous shrinkage of VES-LMC by carrying out simple temperature rise test and early-age shrinkage experiment. Test results are as follows: The latex contributes on the enhancement of the concrete durability but has little effect on its hydration and the accompanied heat of hydration in VES-LMC. Autogenous shrinkage increased with the increase in latex-cement ratio at variable slumps and its pattern followed regularly a logarithmic increase. However, the influence of water-cement ratio and latex-cement ratios for the test specimens at constant slump on early-age autogenous shrinkage property was found to be minor due to the simultaneous effect of the two experimental variables.
초속경 라텍스개질 콘크리트(VES-LMC)는 공용중 교량바닥판 콘크리트 긴급 덧씌우기를 목적으로 개발되었으며, 콘크리트타설 후 3시간 만에 교통개방이 가능하도록 작업성, 내구성 및 강도특성을 만족하도록 특성화된 콘크리트이다. VES-LMC 배합은 고유의 급속경화 특성으로 인해 콘크리트 타설 초기에 높은 수화열을 수반하고, 상대적으로 낮은 물시멘트비로 인해 자기수축에 민감하게 반응할 수 있다. 본 논문에서는 간이수화열과 초기수축 실험을 수행하여 동일슬럼프 조건과 서로 다른 슬럼프 조건에서 라텍스함량 변화가 VES-LMC의 자기수축에 미치는 영향을 평가하였다. 실험결과는 다음과 같다. 라텍스는 콘크리트 내구성 향상에만 기여할 뿐 수화열에 미치는 영향이 매우 작게 나타났다. 서로 다른 슬럼프 조건에서 자기수축은 라텍스함량 증가에 따라 증가하였고, 증가추세는 로그함수의 형태로 나타났다. 그러나 동일 슬럼프조건에서 라텍스함량 변화는 두 가지 실험변수가 동시에 변화하므로 자기수축 특성에 미치는 상관성이 작게 나타났다.