Abstract
Ionic polymer-metal composite (IPMC) actuator generates bending actuation via ion/water flux to the cathode side under an electric field. Polyelectrolytes in IPMC should possess high water-retention capability, proton conductivity, and Young's modulus. In this study. for endowing IPMCs with these properties, Nafion-alumina composite membranes containing $\alpha$- or $\gamma$-aluminas of $4{\sim}8$ wt% were prepared. Mechanical moduli of Nafion-alumina composite membranes were $7{\sim}3$ MPa higher than that of Nafion, with the slight decrease in proton conductivity. At DC 3 V. the actuation performance of the Nafion-$\alpha$-alumina (8 wt%)-IPMC was superior to that of the typical Nafion-IPMC. exhibiting 2.7 times the displacement with an enhanced blocking force. The enhanced actuation performance with the Nafion-$\alpha$-alumina composite membranes was attributed to the higher proton conductivity, the elevated ion/water flux, and the lower interfacial electric resistance of platinum electrodes and membrane, compared with those containing $\gamma$-alumina.
전기활성 고분자 중의 하나인 이온성 폴리머-금속 복합체(ionic polymer-metal composites, IPMC) 작동기는 전압 인가 시 고분자전해질 내부에 존재하는 양이온과 물이 음극 방향으로 이동하면서 변위를 발생시킨다. 이러한 IPMC의 전해질은 높은 보습력, 프로톤 전도도 및 기계적 강도를 지녀야 하며, 이를 위해 본 연구에서는 IPMC의 고분자전해질인 나피온 층에 $\alpha$-, $\gamma$-알루미나를 $4{\sim}8$ wt%의 함량으로 도입하여 나피온-알루미나 복합막을 제조하고 그 특성을 확인하였다. 알루미나의 함량이 증가함에 따라, 나피온 복합막의 프로톤 전도도는 조금씩 감소하는 경향을 보였으며, $\alpha$-알루미나에 비해 $\gamma$-알루미나를 첨가하였을 때 전도도 감소가 더욱 컸다. 나피온-알루미나 복합막의 기계적 모듈러스는 37.16 MPa인 순수 나피온 막에 비해 모든 함량에서 $7{\sim}13\;MPa$ 높았다. 또한 준비된 나피온-알루미나 복합막을 이용하여 IPMC를 제작하였고 직류 3 V의 인가전압 하에서 작동성능을 평가하였다. 나피온-알루미나-IPMC, 특히 8 wt%의 $\alpha$-알루미나가 첨가된 IPMC는 기존 나피온-IPMC에 비해 작동변위는 2.7배 향상되었고 작동력 또한 크게 향상되었다. $\alpha$-알루미나의 첨가에 따른 작동성능의 향상은 $\gamma$-알루미나가 첨가된 복합막에 비해 상대적으로 높은 $\alpha$-알루미나 복합막의 양성자 전도도 그리고 잘 분산된 알루미나 입자 표면에 존재하는 다량의 수분에 의한 이온/물 이동의 용이성, 또한 순수 나피온 막에 비해 전해질 막과 백금전극 사이의 낮은 전기적 저항 때문인 것으로 결론지었다.