Quality Improvement of High Volume Fly Ash Concrete due to Early Strength Gain Admixture

조강형 혼화제에 의한 플라이애시 다량 치환 콘크리트의 품질 향상

The purpose of the study was to improve quality of high volume fly ash concrete. The study evaluated on the possibility of early quality improvement of high volume fly ash concrete with early strength gain admixture ('GA' below) developed by the preceding research. The study regarded applying naphthalene admixture ('NA' below) to mix proportion substituting FA 15 % to be plain. In the event of substituting FA 20, 25 and 30 %, the study compared engineering properties of concrete with plain by applying GA. Because of features of fresh concrete, fluidity falls down when GA is applied. Therefore, its use amount shall be increased. Only, in W/B 60 %, it was beneficial since slump loss was reduced about 35~70 mm than plain. The study could see that AE use should be increased proportionally since air content was reduced by coming from AE absorption operation of unburned coal content included in FA according to an increase in the amount of FA use. Reduction effect of bleeding could be anticipated since the amount of bleeding appeared at least in FA 20 %. Because of hardened concrete, time of setting appeared in the same level as plain when GA was applied. Therefore, it is judged that delay of setting can be reduced. In compressive strength, the study could check the same strength development as plain when GA was applied, having nothing to do with W/B and curing temperature. However, it is thought that we shall pay attention to GA use in the event of FA 30 % substitution. Freezing and melting resistance had less early value than plain. However, it is judged that there will be no problem of frost resistance since there is no a large difference between freezing and melting resistance and plain in overall. In accelerated neutralization, it was analyzed that a problem of weakening in neutralization appointed as a demerit when FA was applied in mass in proportion with GA use could be settled to some extent.

본 연구에서는 FA 다량 치환 콘크리트의 품질 개선 및 기타 품질 향상을 목적으로 선행 연구에서 개발된 조강형 혼화제(GA)로 FA 다량 치환 콘크리트의 품질 향상 가능성을 평가하였다. 실험은 우선 FA 15%를 치환한 배합에 나프탈렌계 혼화제(이하 NA)를 사용한 것을 Plain으로 하였고, FA 20, 25% 및 30%를 치환한 경우, GA를 사용하여 콘크리트의 제반특성을 Plain과 비교 실험 하였다. 굳지 않은 콘크리트 특성으로 유동성은 GA를 사용할 경우 저하하므로 그 사용량을 증가시켜주어야 하는데, 단 W/B 60%의 경우는 Plain 보다 슬럼프 로스가 약 35~70 mm 감소하여 유리한 것으로 나타났다. 공기량은 FA 사용량 증가에 따라 FA에 포함된 미연소탄분의 AE제 흡착작용에 기인하여 감소함으로서 AE제 사용을 비례적으로 증가시켜 주어야함을 알 수 있었다. 블리딩은 FA 20%에서 블리딩 발생량이 가장 적게 나타나 블리딩 저감 효과를 기대할 수 있었다. 경화 콘크리트의 특성으로 응결시간은 GA를 사용한 경우 Plain과 동등한 수준으로 나타나, 응결 지연현상을 줄일 수 있는 것으로 판단된다. 압축강도는 W/B 및 양생온도와 관계없이 GA를 사용한 경우 Plain과 동등한 강도 발현을 확인 할 수 있었으나, FA 30% 치환한 경우는 사용상에 주의가 필요할 것으로 사료된다. 동결융해 저항성은 Plain보다 초기 값이 작게 나타났으나, 전반적으로 큰 차이가 아니기 때문에 내동해성 문제가 없을 것으로 판단된다. 촉진 중성화는 GA를 사용함에 따라, FA를 다량 사용할 경우 단점으로 지적되는 중성화 취약에 대한 문제는 어느 정도 해결 할 수 있을 것으로 분석되었다.