주강의 유화물 형태와 편석에 대한 연구 (I) (Fe-FeS 합금의 제조와 유화물 형태 관찰)

Morphology and Segregation of Sulfide Inclusions in Cast Steels (I) (A Fabrication of Fe-FeS Alloys and the Observation of Their Sulfide Morphology)

  • 박흥일 (부경대학교 대학원 소재프로세스공학과) ;
  • 김지태 (삼영엠텍(주)) ;
  • 김성규 (부경대학교 대학원 소재프로세스공학과)
  • Park, Heung-Il (Department of materials processing engineering, Graduate school, Pukyung National University) ;
  • Kim, Ji-Tae (Samyoung M-Tek Co., Ltd.) ;
  • Kim, Sung-Gyoo (Department of materials processing engineering, Graduate school, Pukyung National University)
  • 발행 : 2009.10.31

초록

In order to investigate the microstructural morphology of the sulfide expected from the Fe-FeS phase diagram, a vacuum-sealed quartz tube where pure iron (99.9%) and sulfur (99.99%) powders were charged was heated upto $1000^{\circ}C$ in the electric resistance furnace, held for 96 hours and quenched in cold water and then, rod specimen was produced. Compositional difference of the sulfur between upper and lower parts of the rod was 7.5wt.% and segregation of the sulfur was gradually increased from the lower part to the upper one of the rod. The rod specimen was divided into three parts by the microstructural morphology of the sulfide. The upper part of the rod specimen revealed single phase FeS intermetallic. In the middle part of the specimen, hyper-eutectic microstructure where primary FeS was precipitated first and then, eutectic of $\alpha$-Fe and FeS was formed in the inter-dendritic region of the FeS. Especially, hypo-eutectic microstructure was appeared in the lower part of the specimen. After primary dendrite of $\alpha$-Fe solidified, FeS dendrite which included small amount of $\alpha$-Fe and FeS eutectic in the inter-dendritic region was formed.

키워드

참고문헌

  1. C. E. Sims, F. B. Dahle, "Effect of Aluminum on the Properties of Medium Carbon Cast steel",Transactions of the American Foundrymen's Association, Vol.46 (1938) 65-132
  2. C. E. Sims, H. A. Saller and F. W. Boulger, "Effects of various deoxidizers on the structures of sulphide inclusions", Transactions, American Foundry Society, 57 (1949) 233-248
  3. C. E. Sims, "The nonmetallic constituents of steel", Transactions of the metallurgical society of AIME, Vol.215 (1959) 367-392
  4. E. T. Turkdogan, S. Lgnatowicz and J. pearson, "The solubility of sulphur in iron and iron manganese alloys", J. of iron and steel institute, (1955) 349-354
  5. H. I. Park et al, "A case study on the solidification behavior and defects of heavy steel castings", J. of the Korean Foundrymen's Society, Vol.26, No.2 (2006) 57-62
  6. J. K. Brimacombe and K. Sopimachi, "Crack formation in the continuous casting of steel", Metallurgical transactions B, Vol.8B (1977) 489-505
  7. C. L. Briant and S. K. Banerji, "Intergranular failure in steel: the role of grain-boundary composition", International metals reviews, No.4 (1978) 164-199
  8. A. Chojecki, I. Telejko and T. Bogacz, "Influence of chemical composition on the hot tearing formation of cast steel", Theoretical and applied fracture mechanics, Vol.27 (1997) 99-105 https://doi.org/10.1016/S0167-8442(97)89529-8
  9. ASM Handbook, Vol. 6 (1997) 88-106 "Cracking phenomena associated with welding"
  10. A. Chojecki, I. Telejko and P. Kozelsky, "Influence of calcium on cracking of steel during the welding or casting process", Theoretical and applied fracture mechanics, Vol.31 (1999) 41-46 https://doi.org/10.1016/S0167-8442(98)00065-2
  11. T. H. Massalski, ASM, Binary alloy phase diagram, Vol.2 (1986) 1103