Abstract
The objective of this study was to investigate potential usage of environmentally friendly building materials, liquid mortar and dry cement mortar mixed with charcoal, based on the test of their physical and chemical properties. From the test results of physical and chemical properties of the liquid mortar mixed with charcoal, liquid mortar containing over 20% of charcoal, the consistency viscosity and the non-volatile content met a standard requirement. Drying time was delayed with increase in charcoal contents in the liquid mortar, however they were fully cured within 60 minutes in all treated levels. Other properties were acceptable at standard requirement. From the results, it was found that the proper charcoal addition level to the liquid mortar was 25%. In the results on dry cement, it was found that samples containing 5% of charcoal showed the maximum compressive strength, whereas samples containing over 20% of charcoal did not reach the minimum requirement of KS standard. Water retention ability constantly increased as the charcoal ratio increased. The conventional dry cement mortar adsorbed 59.5% of it, in the test of adsorption rate on ammonia gas, whereas cement mortar containing 10% of charcoal showed 71.6% of ammonia gas adsorption.
본 연구는 일반 페인트 및 건조시멘트에 목탄을 첨가하여 제조된 건축자재의 제반 물리 화학적 특성 조사를 바탕으로 하여 목탄의 친환경 건축자재 혼합제로서의 활용 가능성을 모색하기 위한 목적으로 수행되었다. 목탄을 포함한 액상몰탈의 물리 화학적 물성 시험결과, 목탄 20% 이상을 포함한 액상몰탈의 경우, 점도에 대한 저항치인 주도와 불휘발분이 품질기준에 적합하였다. 목탄 첨가량이 증가할수록 건조시간은 지연되었으나, 모든 처리구에서 품질기준인 60분 이내에서 건조가 완료되었다. 기타 제반 물성에서는 모든 처리구에서 품질기준을 충족하였다. 이 결과로 볼 때, 액상 몰탈에 대한 적정 목탄 함량은 25%로 판단된다. 건조 시멘트 몰탈에 대한 압축강도는 목탄 5% 첨가구에서 가장 우수하였으며, 20% 이상 첨가구에서는 KS 기준치에 비해 낮은 것으로 조사되었다. 또한 목탄 첨가량 증가로 보수성은 지속적으로 증가하며, 암모니아가스 탈취율의 경우 일반 시멘트 몰탈이 59.5%, 목탄 10% 첨가 시멘트 몰탈은 71.6%의 암모니아를 흡착하였다.