Abstract
A grouting method has been widely used in construction of large-scale structure to reduce permeability and reinforce the ground. If cement and grout material were not mixed well in the injection tip equipment, an opposite flow and interception state of the chemical grouting can occur. McG (Multi-mixing counterflow prevented Grouting, McG) method installed a special grouting device to allow better mixing of the grouting material(above fineness $6,000cm^2/g$) and prevent backward flow. The block of nozzle also diversify powder rate of cement. YSS (Youngil Special Silicate, YSS) that lowers $Na_2O$ and thereby increases durability was developed by gel-forming reaction material. The seepage state and unconfined compressive strength of the injection material using the special injection tip equipment was tested in this study. The results of this study showed that the uniaxial compressive strength, permeability, N-value, TCR and RQD were improved by this method. Engineering characteristics obtained by the special injection tip method will be compared with those by the other method through various field tests from now on.
최근 고속철도, 지하철, 댐, 항만, 고속도로, 도심지의 주상복합건물 등 대형 건설공사가 진행되면서 약액주입공법, 고압분사주입공법, 혼합처리공법 등이 다양하게 적용되고 있으나 침투성, 강도, 내구성, 환경성, 주변지반의 융기, 지하매설물에 대한 영향, 산업폐기물발생 등 많은 문제점이 지적되어 왔다. 이에 본 연구에서는 특수 주입선단장치 및 변성실리케이트 재료를 개발하여 주입재료의 혼합이 용이하고 주입중 주입재의 역류 및 주입노즐의 막힘이 없이 연속작업이 가능하며, 분말도 $6,000cm^2/g$이상인 마이크로시멘트를 사용 침투효과를 증가시켰다. 또한, 겔형성반응재는 내구성과 환경성에 영향을 끼치는 $Na_2O$ 함량을 대폭 낮춘 변성실리케이트를 개발하여 지하수에 의한 용탈현상을 최소화하고, 장기의 고강도, 고침투, 고내구성, 친환경성이 요구되는 곳에 적합한 마이크로 무기질급결재를 개발하여 실용화에 대한 연구를 수행하였다. 연구결과 일축압축강도, 투수성, N치 및 TCR, RQD 등이 개선됨을 알 수 있었으며, 향후 본 연구결과를 바탕으로 특수 주입선단장치를 활용한 다양한 현장적용성 시험을 추후 시행하여 타공법과 공학적 특성을 비교, 검토하고자 한다.