PARTITIONING RATIO OF DEPLETED URANIUM DURING A MELT DECONTAMINATION BY ARC MELTING

  • Published : 2008.10.31
Download PDF
⟨ Previous Next ⟩

Abstract

In a study of the optimum operational condition for a melting decontamination, the effects of the basicity, slag type and slag composition on the distribution of depleted uranium were investigated for radioactively contaminated metallic wastes of iron-based metals such as stainless steel (SUS 304L) in a direct current graphite arc furnace. Most of the depleted uranium was easily moved into the slag from the radioactive metal waste. The partitioning ratio of the depleted uranium was influenced by the amount of added slag former and the slag basicity. The composition of the slag former used to capture contaminants such as depleted uranium during the melt decontamination process generally consists of silica ($SiO_2$), calcium oxide (CaO) and aluminum oxide ($Al_2O_3$). Furthermore, calcium fluoride ($CaF_2$), magnesium oxide (MgO), and ferric oxide ($Fe_2O_3$) were added to increase the slag fluidity and oxidative potential. The partitioning ratio of the depleted uranium was increased as the amount of slag former was increased. Up to 97% of the depleted uranium was captured between the ingot phase and the slag phase. The partitioning ratio of the uranium was considerably dependent on the basicity and composition of the slag. The optimum condition for the removal of the depleted uranium was a basicity level of about 1.5. The partitioning ratio of uranium was high, exceeding $5.5{\times}10^3$. The slag formers containing calcium fluoride ($CaF_2$) and a high amount of silica proved to be more effective for a melt decontamination of stainless steel wastes contaminated with depleted uranium.

Keywords

References

  1. K.L. Hopkinson, A. Bishop, M.T. Cross, J. Harrison and F. Selgas, 'Recycling and reuse of radioactive material in the controlled nuclear sector', EUR18041 EN, European Commission (1998)
  2. D.G. Atteridge, J. Buckentin, J. Carter, H.L. Davis, J. H. Devletian, M.R. Scholl, R.B. Turpin, S.L. Webster, and R.E. Mizia, 'Refining technology for the recycling of stainless steel radioactive scrap metals FY 94 Bi-annual report', WINCO-1224 (1994)
  3. G. Imbard, and S. Rigaud, 'Melting of Cs contaminated ferritic steel from G2/G3 reactors, Marcoule', Proceeding of Technical seminar on melting and recycling of metallic waste materials from decommissioning of nuclear installations, European Commission, Germany, 193 (1993)
  4. R. Anigstein, W.C. Thurber, J.J. Mauro, S.F. Marschke, U.H. Behling, 'Potential recycling of scrap metal from nuclear facilities', Technical support document, U.S. Environmental Protection Agency (2001)
  5. D. Neuschütz, D. Spirin, U. Quade, J. Meier-Kortwig, L. Holappa, M. Hämäläinen, M.A. Heredia Lozano and M.J. Guio Bonany, 'Inadvertent melting of radioactive sources in BOF or EAF: Distribution of nuclides, monitoring, prevention, ISIJ International, 45, 288-295 (2005) https://doi.org/10.2355/isijinternational.45.288
  6. M. Aoyama, Y. Miyamoto, M. Fukumoto, and O. Suto, 'Development of melt refining decontamination technology for low level radioactive metal waste contaminated with uranium', Journal of Physics and Chemistry of Solids, 66 608-611 (2005) https://doi.org/10.1016/j.jpcs.2004.07.020
  7. T. Uda, H. Iba, and H. Tsuchiya, 'Decontamination of uranium contaminated mild steel by melt refining', Nuclear Technology, 73 109-115 (1986) https://doi.org/10.13182/NT86-A16207
  8. B. Heshmatpour and G.L. Copeland, 'Metallurgical aspects of waste metal decontamination by melt refining', Nuclear and Chemical Waste Management, 2 25-31 (1981) https://doi.org/10.1016/0191-815X(81)90004-8
  9. M. Abe, T. Uda, and H. Iba, 'A melt refining method for uranium contaminated steels and copper', In Waste Management, Tucson, AZ 375-378 (1985)
  10. M.R.B. Joanna, B.K. Damkroger, and M.E. Schlienger, 'Radioactive scrap metal decontamination technology assessment report', SAND 96-0902 (1996)
  11. X.W. Ren, U.C. Liu, and Y. Zhang, 'Melt refining of uranium contaminated copper, nickel, and mild steel', Proceeding of the international and topical meeting on nuclear and Hazardous waste management, Spectrum 94, Atlanta, August 14-18, ANS (1994)
  12. P.S. Song, B.Y. Min, W.K. Choi, C.H. Jung, W.Z. Oh, and J.H. Park, 'Melting characteristics of metal wastes in an electric arc furnace', J. Industrial Engineering and Chemistry, 12, 248-254 (2006)
  13. S.A. Worcester, L.G. Twidwell, D.J. Paolini, T.A. Weldon, and R.E. Mizia, 'Decontamination of metals by melt refining/slagging - An annotated bibliography', WINCO-1138, INEL-DOE (1993)
  14. M.E. Schlienger, M. Janna, and B.K. Damkroger, 'Melt processing of radioactive waste: a technical overview', SAND-97-0811C (1997)
  15. E.L. Joyce, B.R. Lally, R.J.Fruehan, and B. Ozturk, 'Liquid Metal Recycle and Waste Treatment : Liquid Metal Melt-Slag Technology Evaluation for MWIP', LAUR Report 93-3026. Submmitted to DOE-EM50 (1995)
  16. B.Y. Min, K. Yong, P.S. Song, W.K. Choi, C.H. Jung, and W.Z. Oh, 'Study in the vitrification of Mixed Radioactive by Plasma Arc Melting,' J. Ind. Eng. Chem, 13, 1 57-64 (2007)
  17. E.T. Turkdogan, Physical Chemistry of High Temperature Technology, Academic Press, New York, 140 (190)
  18. G.L. Copeland, B. Heshmatpour, and R.L. Heestand, 'Melting metal waste for volume reduction and decontamination,' ORNL/TM-7625, Oak Ridge National Laboratory, March (1981)
  19. R.H. Starkey, 'Health aspects of the commercial melting of uranium-contaminate ferrous metal scrap,' Ind. Hyg. J. 178 (1960)
  20. H. Schreiver, G. Balazs, and B. William, 'Structural and redox properties of uranium in C-Mg-Al-silicate glass,' Sci. Basis for Nucl. Waste Management, 3, 109 (1981)
  21. H. Schreiver and G. Balazs, 'The chemistry of uranium in borosilicate glasses. Part1. Simples vase compositions relevant to the immobilization of nuclear waste,' Phys, Chem, Glasses, 23, 139 (1982)
  22. Y.I. Matyunin and S.V. Yudintsev, 'Immobilization of $U_3O_8$ in borosilicate glass in an induction melter with a cold crucible', Atomic Energy, 84 (1998) 173-178 https://doi.org/10.1007/BF02412700