Ni-Ti계 합금 선재의 변태온도 변화에 따른 인장변형 및 회복 특성

Characteristics of Tensile Deformation and Shape Recovery with Transformation Temperature Change in a Ni-Ti Alloy Wire

  • Choi, Y.G. (Dept. of Metallurgy and Materials Engineering, Chosun University) ;
  • Kim, M.S. (Dept. of Metallurgy and Materials Engineering, Chosun University) ;
  • Cho, W.S. (Shinpoong Co. Ltd.) ;
  • Jang, W.Y. (Dept. of Metallurgy and Materials Engineering, Chosun University)
  • 투고 : 2008.11.14
  • 심사 : 2008.11.24
  • 발행 : 2008.11.30

초록

The tensile deformation and shape recovery behaviors were studied in Ni-Ti shape memory wires showing different transformation characteristics by annealing at $200{\sim}600^{\circ}C$. Both R phase ${\rightarrow}$ B19' martensitic transformation at lower temperature and B2 ${\rightarrow}$ R phase transformation at higher temperature occurred in the shape memory wires annealed at $200{\sim}500^{\circ}C$. Transformation temperature and heat flow of B19' martensite increase but those of R phase main almost constant even with increasing annealing temperature. In the case of wires annealed and then cooled to $20^{\circ}C$, plateau on stress-strain curves in tensile testing can be observed due to the collapse of R phase variants and the formation of deformation-induced B19' martensite. In the case of wires annealed and then cooled to $-196^{\circ}C$, however, plateau on stress-strain curves does not appear and stress increases steadily with increasing tensile deformation. Comparing shape recovery rate with cooling temperature after annealing, shape recovery rate of the wire cooled to $20^{\circ}C$ is higher than that of the wire cooled to $-196^{\circ}C$ after annealing, and maximum shape recovery rate of 95% appears in the wire annealed at $400^{\circ}C$ and then cooled to $20^{\circ}C$. $R_s$ and $R_f$ temperatures measured during shape recovery tests are higher than $A_s$ and $A_f$ temperatures measured by DSC tests even at the same annealing temperature.

키워드

참고문헌

  1. J. Van Humbeeck : Mater. Sci. and Eng., A273-275 (1999) 134
  2. G. S. B. Kelly, B. N. Agrawal, D. C. Lam and T. S. Srivatsan : J. Mater. Eng. & Performance 9(3) 2000
  3. C. Cocud, A. Price, A. Jnifene and H. Naguib : Int. J. Mech. Mater. Eds, in press, 2007
  4. W. Liang, D. J. Srolovitz and M. Zhou : J. Mech. & Phys. Solids 55 (2007) 1729 https://doi.org/10.1016/j.jmps.2007.01.001
  5. Z. Nishiyama : Martensitic Transformations, New York Academic Press (1978) 269
  6. T. Fukuda, T. Saburi, K. Doi and S. Nenno : Mater. Trans JIM, 33 (1992) 271 https://doi.org/10.2320/matertrans1989.33.271
  7. T. Saburi, S. Nenno, Y. Nishimoto and M. Zeniya : J. Iron and Steel Inst., 72 (1986) 571 https://doi.org/10.2355/tetsutohagane1955.72.6_571