Characteristics and Properties of Fluoro/Silicone Rubber Blend System

불소/실리콘 고무 블렌드의 특성과 물성

  • Lee, Jin-Kook (Department of Polymer Science & Engineering, Pusan National University) ;
  • Song, Hwan-Jae (Department of Polymer Science & Engineering, Pusan National University) ;
  • Kim, Mi-Ra (Department of Polymer Science & Engineering, Pusan National University)
  • 이진국 (부산대학교 응용화학공학부) ;
  • 송환제 (부산대학교 응용화학공학부) ;
  • 김미라 (부산대학교 응용화학공학부)
  • Received : 2008.07.30
  • Accepted : 2008.09.23
  • Published : 2008.09.30
Download PDF
⟨ Previous Next ⟩

Abstract

In this study, silicone rubber (SR40) and fluororubber (FKM) mixture blends were prepared by various weight percentages, and their properties were characterized. The crosslinking rate increased as the contents of SR40 due to the crosslinking agent in SR40. As contents of FKM increase in SR40/FKM blends, thermal decomposition temperature of blends increased. When SR40/FKM blend ratio was at 50/50, the thermal decomposition stabilization was higher than that of pure SR40. The contact angle of SR40/FKM blend increased as the increase of SR40 contents in blend. All composition of SR40/FKM blends showed typical phase separation morphology. As the contents of SR40 increase in SR40/FKM blend, the degree of separation in SR40/FKM blends also increased.

본 연구는 Silicone rubber (SR40)과 Fluororubber (FKM)을 여러 가지 무게비로 하여 블렌드를 제조하였고 그 특성을 고찰하였다. 블렌드의 가교 거동은 SR40의 함량이 증가함에 따라 SR40 내의 가교제에 의해 가교 속도는 빨라졌다. 블렌드에서 FKM의 함량이 증가하면, 열분해 온도가 증가는 경향이 있고 SR40/FKM 블렌드 비율이 50/50일 때 순수한 SR40보다 높은 열안정성을 나타내었다. 표면 발수성의 척도인 접촉각을 측정한 결과, SR40의 함량이 증가할수록 블렌드의 접촉각은 증가하는 것을 확인하였다. 또한, 제조한 블렌드들은 모든 조성에서 전형적인 상분리의 모폴로지를 나타내는 것을 확인할 수 있었고, SR40의 비율이 증가할수록 상분리 정도가 증가하는 것을 확인할 수 있었다.