Abstract
Purpose: This research is that $V_2O_5$ cathode's composition is possible in low temperature. Methods: Transparent in visible spectra range and crystallographically amorphous $V_2O_5$ thin films were prepared by simple vacuum thermal evaporation on soda-lime-silica slide glass substrate. After annealing at 100$^{\circ}C$, 150$^{\circ}C$ and 200$^{\circ}C$ for 10 minutes in air, the surface morphology and the fracture-cross section of the films were investigated by field emission - scanning electron microscope. Transmittance in visible spectra range and surface roughness of the films were analyzed by ultra violet - visible spectrophotometer and scanning probe microscope, respectively. Results: As the increase of annealing temperature from 100$^{\circ}C$ to 150$^{\circ}C$ and 200$^{\circ}C$, transmittance of the $V_2O_5$ films decreased. Optical properties will be fully discussed on the basis of the surface morphological results. Conclusions: Optical transmissivity was superior in case of 100$^{\circ}C$, and could make amorphous $V_2O_5$ thin film that surface quality of thin film did homogeneity.
목적: 본 논문은 저온에서 $V_2O_5$의 cathode의 합성이 가능하다는 것이다. 방법: 간편한 진공 열증착법을 이용하여, 현미경용 소다 라임 실리카 슬라이드 기판위에 가시영역에서 투명하고 결정학적으로 비정질인 $V_2O_5$ 박막을 제조하였다. 100, 150 및 200$^{\circ}C$로 10분간 열처리가 완료된 박막의 표면미세구조와 파단면을 전계방사 주사형 전자현미경으로 분석하였다. 박막의 가시영역에서의 투과율과 표면 거칠기를 ultra violet-visible spectrophotometer와 Scanning probe microscope로 각각 분석하였다. 결과: 열처리 온도가 100$^{\circ}C$에서 150 및 200$^{\circ}C$로 증가함에 따라, 박막의 투과율은 감소하는 경향을 보였다. 박막의 광학적 특성은 표면미세구조적 결과를 바탕으로 토론될 것이다. 결론: 100$^{\circ}C$인 경우 광학적 투과율이 우수하고, 박막의 표면특성이 균질한 비정질 $V_2O_5$ 박막을 제조할 수 있었다.