Abstract
As buildings are becoming taller and longer-spanned, the requirements of high-strength and reliable steels are becoming increasingly stringent. Structural steels, however, acquire significantly different mechanical properties when their strength becomes higher. In this study, the mechanical properties, welding characteristics, and conformities of the 600MPa-grade high-strength steel were tested. The 600MPa-grade steel plates exhibited stable criterion strengthvalues and showed low carbon equivalents (${\mathcal{Ceq}}$) and composition (${\mathcal{Pcm}}$) as well as excellent welding hardness. In the tensile strength test, all the specimens were found to have strengths of over 600MPa. In the Sharphy impact test, the impact-absorbed energy of the V-notch specimens was shown to be 47J at the KS limit. Moreover, the maximum hardness of the specimens in the weld-heat-affected zone at a normal temperature was the same as that before welding. Their weld metal properties, however, were found not to be as good as those of high-strength steel. As such, the details of high-strength steel must be determined.
건축물이 초고층화, 장스팬화가 되어갈수록 고강도, 신뢰성이 우수한 강재의 사용요구가 증대되고 있다. 그러나 강재가 고강도화가 되어갈수록 일반강재와는 다른 기계적 특성을 갖게 된다. 본 연구에서는 600MPa급 고강도 강재에 대한 건축구조용 강재로서의 적합성, 용접성 및 기계적 특성을 파악하기 위하여 소재특성 및 용접부 특성을 평가하였다. 화학시험결과, 대상강재는 낮은 탄소당량(${\mathcal{Ceq}}$) 및 용접갈라짐 감수성 조(${\mathcal{Pcm}}$)성을 가진 것으로 나타났으며, 인장시험결과로부터 모든 시험체의 항복강도는 설계기준강도를 만족하는 것과 인장강도가 600MPa이상인 것을 확인하였다. 충격시험결과, 모든 시험체는 KS 규격 값인 47J이상을 나타내었다. 또한 용접부 최고경도시험에서도 상온과 예열시의 경화정도가 큰 차이가 없는 것으로 나타났다. 그러나 용착금속 경우 강재의 성능에 미치지 못하여 고성능 고강도 강재용 용착금속의 개발 및 용접조건을 세밀히 파악할 필요가 있는 것으로 판단된다.