Preparation of Core-Shell Structured BaTiO3 Powder Via Coating of Cr2O3 and Mn2O3

Cr2O3 및 Mn2O3의 코팅에 의한 Core-Shell 구조의 BaTiO3 분말 제조

  • Received : 2007.10.01
  • Accepted : 2007.10.19
  • Published : 2008.02.28
Download PDF
⟨ Previous Next ⟩

Abstract

Core-shell structured $BaTiO_3$ powders were produced via nano-coating of $Cr_2O_3$ and $Mn_2O_3$ to barium titanate powder system for MLCCs. From preliminary experiments, the optimal solution reaction condition employing using $KMnO_4$, $K_2Cr_2O_4$ and sulfur was established. Not only powders of $Cr_2O_3$ and $Mn_2O_3$ were synthesized but also their coating on $BaTiO_3$ powders were peformed under the same reaction condition. The coating was carried out in two ways, one-step and two-step, and its results were characterized for comparison. Conclusively speaking, two oxide additives were coated onto the $BaTiO_3$ powder surface with high quality and excellent reaction yield even under mild condition, which indicates that the contents as well as the properties of additive shell layer can be precisely controlled with rather ease.

본 연구에서는 MLCC용 $BaTiO_3$에 첨가되는 $Cr_2O_3$와 $Mn_2O_3$의 나노코팅에 의한 core-shell 구조의 $BaTiO_3$ 분말을 제조하였다. 예비실험을 통해서 $KMnO_4$ 및 $K_2Cr_2O_4$ 그리고 sulfur를 사용하는 최적의 액상반응조건이 확립되었다. 본 연구에서는 두 첨가제 분말을 합성하였고 동일한 반응조건으로 두 첨가제를 $BaTiO_3$ 분말표면에 코팅하였다. 코팅은 one-step과 two-step의 두 방법으로 구분하여 시행하였고 그 결과를 분석 비교하였다. 결론적으로 말해서, $Cr_2O_3$와 $Mn_2O_3$의 두 첨가제는 용이한 반응조건에서 높은 수율로 우수한 품질의 코팅막을 형성하므로써, 첨가제 함량과 코팅막 특성의 정밀한 조절이 용이함을 보여주었다.

Keywords

Acknowledgement

Supported by : 인제대학교

References

  1. Jiang, S., Zhou, D., Gong S. and Guan, X., "Effect of Heat-treatment under Oxygen Atmosphere on the Electrical Properties of $BaTiO_3$ Thermistor,"Microelec. Eng., 66(1), 896-903(2003). https://doi.org/10.1016/S0167-9317(02)01018-3
  2. Thomas, R., Dube, D. C., Kamalasanan, M. N. and Chandra, S., "Optical and Electrical Properties of BaTiO3 Thin Films prepared by Chemical Solution Deposition," Thin Solid Films, 346(5), 212-225(1999). https://doi.org/10.1016/S0040-6090(98)01772-6
  3. Canulescu, S., Dinescu, D., Epurescu, G., Matei, D. G., Grigoriu, C., Craciun, F., Verardi, P. and Dinescu M., "Properties of BaTiO3 Thin Films deposited by Radio Frequency Beam Discharge Assisted Pulsed Laser Deposition,"Mat. Sci. Eng. B, 109(6), 160- 166(2004). https://doi.org/10.1016/j.mseb.2003.10.103
  4. Lines, M. E. and Glass, M., Principles and Applications of Ferroelectric and Related Materials, Clarendon, Oxford(1982).
  5. Park, Y., Kim, Y. H. and Kim, H. G., "The Effect of Grain Size on Dielectric Behavior of $BaTiO_3$ based X7R Materials," Mater. Lett., 28(9), 101-106(1996). https://doi.org/10.1016/0167-577X(96)00054-7
  6. Conley, J., "Aerosol Delivery of Liposome-encapsulated Ciprofloxacin: Aerosol Characterization and Efficacy against Francisella Tularensis Infection in Mce," Antimicrobial Agents and Chemotherapy, 32(6), 1288-1292(1997).
  7. Matijevic, E., "Colloid Science in Ceramic Powders Preparation," in Materials Science Monographs vol. 38A, High Tech Ceramics Part A, 441-458(1990).
  8. Gherardi, P. and Matijevic, E., "Interaction of Precipitated Hematite with Preformed Colloidal Titania Dispersions," J. Colloid Interface Sci., 109(1), 57-61(1986). https://doi.org/10.1016/0021-9797(86)90281-X
  9. Kratohvil, S. and Matijevic, E., "Preparation and Properties of Uniform Coated Inorganic Colloidal Particles: Silica on Iron," Adv. Ceram. Mater., 118, 506-511(1987).
  10. Garg, A. and Matijevic, E., "Preparation and Properties of Uniform Coated Inorganic Colloidal Particles. III. Zirconium Hydrous Oxide on Hematite," Langmuir, 4(11), 38-42(1988). https://doi.org/10.1021/la00079a006
  11. Kawahashi, N. and Matijevic, E., "Preparation and Properties of Uniform Coated Colloidal Particles. V. Yttrium Basic Carbonate and Polystyrene Latex," J. Colloid Interface Sci., 138(9), 534-542 (1990). https://doi.org/10.1016/0021-9797(90)90235-G
  12. Aiken, B. and Matijevic, E., "Preparation and Properties of Uniform Coated Inorganic Colloidal Particles. IV. Yttrium Basic Carbonate and Yttrium Oxide on Hematite," J. Colloid Interface Sci., 126(12), 645-650(1988). https://doi.org/10.1016/0021-9797(88)90168-3
  13. Haq, I. and Matijevic, E., "Preparation and Properties of Uniform Coated Inorganic Colloidal Particles," J. Colloid Interface Sci., 192(8), 104-113(1997). https://doi.org/10.1006/jcis.1997.5002
  14. Caruso, F., "Nanoengineering of Particle Surfaces," Adv. Mater 13, 1-17(2001).
  15. Wang, X. and Li, Y., "Hydrothermal Reduction Route to $Mn(OH)_2$ and $MnCO_3$ Nanocrystals," Mater. Chem. Phys., 82(11), 419-422 (2003). https://doi.org/10.1016/S0254-0584(03)00263-3
  16. Armstrong, A. R. and Bruce, P. G., "Synthesis of Layered LiMnO2 as an Electrode for Rechargeable Lithium Batteries," Nature, 381(6), 499(1996). https://doi.org/10.1038/381499a0
  17. Lee, W.-H. and Su, C.-Y., "Improvement in the Temperature Stability of a BaTiO3-based Multilayer Ceramic Capacitor by Constrained Sintering," J. Am. Ceram. Soc., in press, 90(10), 3345-3348 (2007). https://doi.org/10.1111/j.1551-2916.2007.01900.x
  18. Tsuzuki, T. and McCormick, P. G., "Synthesis of Cr2O3 Nanoparticles by Mechano-chemical Processing," Acta Mater., 48(6), 2795- 2801(2000). https://doi.org/10.1016/S1359-6454(00)00100-2
  19. Onjia, A. E., Milonjic, S. K., Cokesa, Dj., Comor, M. and Miljevic, N., "Characterization of Colloidal Chromia Particles Obtained by Forced Hydrolysis," Mat. Res. Bull., 38(7), 1329-1339(2003). https://doi.org/10.1016/S0025-5408(03)00137-5
  20. Blesaa, M. A., Magaz, G., Salfity, J. A. and Weisz, A. D., "Structure and Reactivity of Colloidal Metal Oxide Particles Immersed in Water," Sol. State Ionics, 101-103(11), 1235-1241(1997). https://doi.org/10.1016/S0167-2738(97)00414-1