인장전단시험을 이용한 TRIP1180강의 계면파단특성 평가

Evaluation of Resistance Spot Weld Interfacial Fractures in Tensile-Shear Tests of TRIP 1180 Steels

  • 박상순 (동의대학교 신소재공학과) ;
  • 최영민 (POSCO 기술연구소 자동차소재연구그룹) ;
  • 남대근 (한국생산기술연구원 동남권 기술지원본부) ;
  • 김영석 (한국생산기술연구원 동남권 기술지원본부) ;
  • 유지훈 (한국기계연구원 부설 재료연구소) ;
  • 박영도 (동의대학교 신소재공학과)
  • Park, Sang-Soon (Dept. of Advanced Material Engineering, Dong-eui University) ;
  • Choi, Young-Min (Automotive Steel Products Research Group, Technical Research Labs., POSCO) ;
  • Nam, Dae-Geun (Division for Dongnam Area Technology Service, Korea Institute of Industrial Technology) ;
  • Kim, Young-Seok (Division for Dongnam Area Technology Service, Korea Institute of Industrial Technology) ;
  • Yu, Ji-Hun (Dept. of Powder Materials Research, Korea Institute of Materials Science) ;
  • Park, Yeong-Do (Dept. of Advanced Material Engineering, Dong-eui University)
  • 발행 : 2008.12.31

초록

The weldability of resistance spot welding of TRIP1180 steels for automobile components investigated enhance in order to achieve understanding of weld fracture during tensile-shear strength (TSS) test. The main failure modes for spot welds of TRIP1180 steels were nugget pullout and interfacial fracture. The peak load to cause a weld interfacial failure was found to be related to fracture toughness of the weld and the weld diameter. Although interfacial fracture occurred in the spot welded samples, the load-carrying capacity of the weld was high and not significantly affected by the fracture mode. Substantial part of the weld exhibits the characteristic dimple (or elongated dimple) fractures on interfacial fractured surface also, dimple fracture areas were drawmatically increased with heat input which is propotional to the applied weld current. In spite of the high hardness values associated with the martensite microstructures due to high cooling rate. The high load-carrying ability of the weld is directly associated with the area of ductile fracture occurred in weld. Therefore, the judgment of the quality of resistance spot welds in TRIP1180 steels, the load-carrying capacity of the weld should be considered as an important factor than fracture mode.

키워드

참고문헌

  1. B. Yan, H. Zhu, SH. Lalam: Spot Weld Fatigue of Dual Phase Steels, SAE technical paper series, 1 (2004), 0511
  2. Yuh J. Chao: Ultimate Strength and Failure Mechanism of Resistance Spot Weld Subjected to Tensile, Shear, or Combined Tensile/Shear Loads, Journal of Engineering Materials and Technology, 125 (2003), 125-132 https://doi.org/10.1115/1.1555648
  3. T. B. Hilditch, J. G. Speer and D. K. Matlock: Effect of susceptibility to interfacial fracture on fatigue properties of spot-welded high strength sheet steel, Materials & Design, 28 (2007), 2566-2576 https://doi.org/10.1016/j.matdes.2006.10.019
  4. Marcio Milititsky, Eric Pakalnines: On Characteristics of DP600 Resistance Spot Welds, SAE technical paper series, 1 (2003), 0520
  5. B Girvin, W Peterson, J Gould: Development of Appropriate Spot Welding Practice for Advanced High Strength Steels (TRP 0114), American Iron and Steel Institute, 27 (2007), A10-A17
  6. J. Y. Baek, J. G. Lee, S. H. Rhee: A Study of Dynamic Characteristic for Resistance Spot Welding Process Using Servo-gun System, Journal of KWS, 23-3 (2005), 40-46. (in Korea)
  7. T. H Kim, H. S. Park, Y. S. Lee, S. H. Rhee: A Strudy of TRIP Steel Weldability Evaluation for Light Body Car in Resistance Spot Welding, Proc. J. KSAE, 2 (2003), 1239-1246. (in Korea)
  8. D. J. Radakovic, M. Tumuluru: Predicting Resistance Spot Weld Failure Modes in Shear Tension Tests of Advanced High-Strength Automotive Steels, American Welding Journal, 87-4 (2008), 96-s to 105-s
  9. M. Marya, X. Q. Gayden: Development of Requirements for Resistance Spot Welding Dual-Phase(DP600) Steels Part 1-The Causes of Interfacial Fracture, American Welding Journal, 84-11 (2005), 172-s to 182-s
  10. Xin Sun, Elizabeth V. Stephens, Mohammad A.Khaleel: Effects of fusion zone size and failure mode on peak load and energy absorption of advanced high strength steel spot welds under lap shear loading conditions, Engineering Failure analysis, 15 (2008), 356-367 https://doi.org/10.1016/j.engfailanal.2007.01.018
  11. K. C. Kim, J. H. Cha, H. S. Park: Resistance Spot Weldability of Coated Steels for Automobile Applications, Kor. Journal of Materials Research, 14-4 (2004), 239-245. (in Korea) https://doi.org/10.3740/MRSK.2004.14.4.239
  12. S. S .Park, S. M. Lee, Y. M. Choi, N. H. Kang, J. H. Yu, Y. S. Kim, Y. D. Park: Evaluation of Resistance Spot Weld Interfacial Fractures in Tensile-Shear tests of TRIP590 Steels, J. Kor. Inst. Met. & Mater, 46-10 (2008). (in Korea)
  13. AWS D8.9-97: Recommended Practices for Test Methods for Evaluating the Resistance Spot Wedling Behavior of Automotive Sheet Steel Materials, AWS, 33-34
  14. Hongyan Zhang, Jacek Senkara: Resistance welding: Fundamentals and Applications, Taylor & Francis Group, 2006, 70-79
  15. AK De, JG Speer, DK Mattock: Color Tint-Etching for Multiphase Steels, Advanced Materials & Processes, 161(2003) 27-30
  16. M. Tumuluru: The Effect of Coatings on the Resistance Spot Welding Behavior of 780MPa Dual-Phase Steel, American Welding Journal, 86-6 (2007), 161s-169s

피인용 문헌

  1. Understanding the factors controlling the interfacial failure strength of advanced high-strength steel resistance spot welds: hardness vs. fracture toughness vol.23, pp.6, 2018, https://doi.org/10.1080/13621718.2017.1421303