The lead zirconate titanate (PZT) powders were synthesized to make the piezoelectric ceramics in low temperature as low as $900^{\circ}C$. To investigate the influence of additives on sintering of PZT, two kinds of sintering aids were made as follows; $wB_2O_3-xBi_2O_3-zCuO$and LiBiO2-CuO. The sintering aid, $1{\sim}3$ wt.% $LiBiO_2-CuO$, was added into these PZT powders and the specimens were fired at temperature in the range of $800{\sim}1200^{\circ}C$. The highest density was shown in the specimen with 1 wt.% $LiBiO_2-CuO$ as additive at temperature of $900^{\circ}C$. The sintered specimen were analyzed by X-ray diffraction(XRD) and scanning electron microscopy (SEM) was utilized to observe the microstructure, especially the densified morphology of specimens. In the XRD pattern, the well-crystallized PZT phase could be obtained in consequence of firing at $900^{\circ}C$. The scanning electron microscopy(SEM) was utilized to observe the structure of specimens after firing at $900^{\circ}C$. The densified perovskite structure of $PbZrTiO_3$ could be obtained by sintering at temperature as low as $900^{\circ}C$. The high sinterability of PZT ceramics was attributed to the low formation temperature of the liquid phase of additives.
저온 소결용 압전 세라믹 소결체의 치밀화에 미치는 첨가제의 영향을 조사하기 위하여 $PbZrTiO_3$(PZT) 분말을 제조하였으며, 이 PZT 분말을 이용하여 제조한 압전 세라믹스의 치밀화에 미치는 첨가제의 영향을 조사하였다. 첨가제는 $wB_2O_3-xBi_2O_3-zCuO$와 $LiBiO_2-CuO$ 두 종류가 제조되었으며 이 들 첨가제의 양을 변화 시켜 효과를 조사하였다. PZT 분말에 소결조제로서 1wt.% 의 $LiBiO_2-CuO$를 첨가하여 시편을 제조한 후, $800{\sim}1200^{\circ}C$까지의 온도 범위에서에서 소결한 결과 $900^{\circ}C$에서 최고의 소결밀도를 나타내었다. 소결된 압전체의 결정상을 분석하기 위하여 X-선회절분석을 시행하였으며, $900^{\circ}C$의 저온에서 소결한 $PbZrTiO_3$의 시편의 미세조직을 관찰하기 위하여 주사전자현미경(SEM)을 이용하였다. X-선 회절분석에서는 잘 발달된 PZT 상이 나타났으며, SEM 관찰 결과 평균입경은 $2{\sim}4\;{\mu}m$의 페로브스카이트 결정으로 균일하고 치밀한 조직을 나타내었으며, 높은 소결성은 첨가제에 의한 액상소결에 기인한다.