EFFECT OF SOFT-START CURING ON THE CONTRACTION STRESS OF COMPOSITE RESIN RESTORATION POLYMERIZED WITH LED AND PLASMA CURING UNIT

LED와 플라즈마 광원의 완속기시 광중합 방식이 복합레진의 수축응력에 미치는 영향

Effect of Soft-start curing on the contraction stress of composite resin restoration polymerized with LED and plasma curing unit The purpose of this study was to evaluate the influence of soft-start light curing on contraction stress and hardness of composite resin. Composite resin (Filtek $Z-250^{TM}$, 3M ESPE, USA) was cured using the one-step continuous curing method with three difference light sources ; conventional halogen light ($XL3000^{TM}$, 3M ESPE, USA) cure for 40 seconds at $400 mw/cm^2$, LED light (Elipar Freelight $2^{TM}$, 3M-ESPE, USA) cure for 20 seconds at $800\;mW/cm^2$ a and plasma arc light ($Flipo^{TM}$, LOKKI, France) cure for 12 seconds at $1300 mW/cm^2$. For the soft-start curing method ; LED light (Elipar Freelight $2^{TM}$, 3M-ESPE, USA) cure exponential increase with 5 seconds followed by 17 seconds at $800\;mW/cm^2$ and plasma arc light ($Flipo^{TM}$, LOKKI, France) cure 2 seconds light exposure at $650\;mW/cm^2$ followed by 11 seconds at $1300\;mW/cm^2$. The strain guage method was used for determination of polymerization contraction. Measurements were recorded at each 2 second for the total of 800 seconds including the periods of light application. Obtained data were analyzed statically using Repeated measures ANOVA, One way ANOVA, and Tukey test. The results of present study can be summarized as follows: 1. Composite resin restoration showed transient expansion just after irradiation of curing light. Contraction stress was increased rapidly at the early phase of polymerization and reduced slowly as time elapsed (P<0.05). 2. Contraction stress was not revealed significant difference between Halogen curing light groups and LED and Plasma Light curing with soft-start group (P>0.05). 3. LED and Plasma Light curing with soft-start showed lower contraction stress than the one-step continuous light curing (P<0.05).

본 연구는 LED와 플라즈마 광원의 복합레진의 중합시 완속기시 중합방식(soft-start curing)이 수축응력에 미치는 효과를 비교, 평가하고자 하였다. 할로겐 광원으로 40초간 조사하여 복합레진을 중합한 경우와 LED와 플라즈마 광원의 단일광도 중합방식과 완속기시 중합방식으로 할로겐 40초 동안의 광에너지와 총량이 동일하도록 조사시간을 설정하였고 수축응력은 스트레인 게이지(Strain gauge)를 사용하여 측정하였다. 발생되는 수축응력을 비교, 분석 및 평가한 결과 다음과 같은 결론을 얻었다. 1. 모든 군에서 중합 후 200초까지 수축응력이 급격하게 증가하였으나 이후 마지막 측정시간인 800초까지 완만한 증가를 보였다(P<0.05). 2. LED와 플라즈마 광원의 완속기시 중합방법이 단일광도 중합방법에 비해 수축응력이 낮게 나타났다(P<0.05). 3. 할로겐 광원과 LED와 플라즈마 광원의 완속기시 중합의 수축응력 비교에는 유의차가 없었다(P>0.05). 완속기시 중합 방식을 사용할 경우 단일광도 중합 방식보다 수축응력을 감소시킬 수 있어 임상적으로 고광도 광원인 LED와 플라즈마 광원의 경우 완속기시 중합 방식의 사용이 유리하다고 보여진다. 그러나 완속기시 중합시 불충분한 중합을 방지하기 위해서는 완속기시를 보완하는 추가적인 중합시간이 요구될 것으로 사료된다.