Abstract
The thermal and magnetic properties of amorphous (FeCo)SiBNb ribbon alloys with high glass forming ability have been investigated. The glass forming ability was enhanced by Co substitution in amorphous ($Fe_{1-X}Co_X)_{72}Si_4B_{20}Nb_4$ alloys with the thickness of about $40{\mu}m$. With the increase in Co content, the temperature range of supercooled liquid phase increased indicating the high glass forming ability of the Co-added alloys. Further the ac permeability increased, and the core loss decreased considerably by Co substitution, while small change in $B_8$ (magnetic flux density at 800 A/m) was observed. The frequency characteristics of permeability deteriorated as compared to conventional amorphous ribbon alloys with the thickness of about $20\;{\mu}m$ due to the increased skin effect.
큰 비정질 형성능을 가지는 FeSiBNb 비정질 리본 합금의 열적 및 자기적 특성에 미치는 Co의 첨가 효과에 대하여 연구되었다. 두께 $40\;{\mu}m$의 비정질$(Fe_{1-X}Co_X)_{72}Si_4B_{20}Nb_4(x=0{\sim}0.5)$ 합금에 대한 열분석 결과, Fe에 대한 Co의 치환량이 증가할수록 과냉각 액상의 존재 온도 범위가 넓어져 비정질 형성능이 증가하는 것으로 평가되었다. 또 Co 농도의 증가에 따라 약간의 $B_8$(800A/m에서의 유도 자속밀도)의 감소가 얻어지나, 투자율이 현저하게 증가하고 철손이 크게 감소하는 경향을 나타내었다. 한편 두께가 두꺼운 상기 비정질 합금의 교류 투자율의 주파수 특성은 와전류에 의한 표피 효과의 증대 때문에 $20\;{\mu}m$ 정도의 두께를 가지는 통상의 비정질 리본 합금에 비해 열화되는 것으로 나타났다.