Preparation of Lightweight Aerated Concrete and Characteristic Analysis of Foaming Agent

경량기포콘크리트의 제조 및 기포제의 특성분석

  • Yim, Going (Dept. Nanopolym. Mat. Eng. Col. of Eng. Pai Chai University) ;
  • Yim, Chai-Suk (Hosung Chemex Co., R&D Center, H.I.T., Hanyang University)
  • 임굉 (배재대학교 공과대학 나노고분자재료공학과) ;
  • 임재석 (호성케멕스㈜ 중앙연구소)
  • Published : 2006.12.31

Abstract

Shrinkage may cause cracking in concrete. In practice such cracking must be considered in most concrete applications because, under normal conditions, drying of the concrete is unavoidable, and when drying takes place shrinkage occurs. Cracked concrete is an inferior concrete because it is weaker, more permeable, and more susceptible to chemical attack. The development of the strength of LAC with aging depends on a few factors such as type of the cement, W/C ratio, curing conditions and periods. The higher the strength of LAC, the lower the possibility of shrinkage cracking. Hence, the strength of LAC in the hypocaust system depends to a large extent on the effect of cracking decrease of the antifoaming rate to drying shrinkage in cement.

수축은 콘크리트에 균열을 발생시키는 경우도 있다. 일반적 조건하에서는 콘크리트의 건조를 피할 수 없으며 건조가 일어나면 수축이 생기므로 대부분의 콘크리트 적용분야에서는 실제로 이와 같이 균열발생을 고려하여야 한다. 균열이 발생한 콘크리트는 균열이 없는 콘크리트에 비하여 강도가 약하고 투과성이 크며 화학적 침식의 영향을 받기 쉽다. 또 재령의 경과에 따라 경량기포콘크리트의 강도발현은 기포제의 종류, 물과 시멘트와의 비, 양생조건 및 기간 등과 같은 인자에 의존하고 있다. 경량기포콘크리트의 강도가 높으면 높을수록 수축에 의하여 균열이 발생할 가능성이 감소한다. 그러므로 온돌구조용으로의 경량기포콘크리트의 강도는 소포율과 시멘트의 건조수축과의 균열저감효과에 크게 의존된다.

Keywords