Abstract
Granulated Blast Furnace Slag (GBFS) is produced in the manufacture process of pig-iron and shows a similar particle formation to that of natural sea sand and also shows light weight, high shear strength, well permeability, and especially has a latent hydraulic property by which GBFS is solidified with time. Therefore, when GBFS is used as a backfill material of quay or retaining walls, the increase of shear strength induced by the hardening is presumed to reduce the earth pressure and consequently the construction cost of harbor structures decreases. In this study, using the model sand box (50 cm$\times$50 cm$\times$100 cm), the model wall tests were carried out on GBFS and Toyoura standard sand, in which the resultant earth pressure, a wall friction and the earth pressure distribution at the movable wall surface were measured. In the tests, the relative density was set as Dr=25, 55 and 70% and the wall was rotated at the bottom to the active earth pressure side and followed by the passive side. The maximum horizontal displacement at the top of the wall was set as ${\pm}2mm$. By these model test results, it is clarified that the resultant earth pressure obtained by using GBFS is smaller than that of Toyoura sand, especially in the active-earth pressure.
고로 수쇄슬래그는 선철의 제철과정에서 생산되는 부산물로서 자연 해성모래와 유사한 입자형상을 가지고 경량이며 큰 전단강도와 투수성을 나타낸다. 특히, 고로 수쇄슬래그는 시간경과와 더불어 경화하는 잠재수경성을 가진다. 따라서 고로 수쇄슬래그가 안벽이나 옹벽의 뒷채움 재료로 사용 되어졌을 때, 경화에 의한 전단강도의 증가로 토압감소가 기대되며, 결과적으로 항만구조물의 건설비용이 감소하게 된다. 본 연구에서는 모형토조를 이용하여 고로 수쇄슬래그와 Toyoura sand에 대해 토압, 벽 마찰력, 가동벽체 표면에서의 토압분포를 측정하는 모형실험을 실시하였다. 실험에서 상대밀도는 25%, 55% 및 70%로 설정하였으며 벽체는 저점을 중심으로 주동 및 수동토압측으로 회전시켰다. 벽체 상부에서의 최대 수평변위는 ${\pm}2mm$로 설정하였다. 모형실험 결과, 고로 수쇄슬래그에서 얻어진 주동토압이 Toyoura sand보다 작음을 알았다.