Abstract
In this study, fluorine-silicate hybrid type crack reducing agent(FS) consisted of fluorine and silicate compounds applied to concrete mix(specification : 25-30-18) between 0.5% and 2.0% at intervals of 0.5% based on cement weight. Experiments for material properties of concrete such as slump, air content and bleeding with elapsed time were performed. Experiment and elucidation for shrinkage crack resistance as well as adiabatic hydration temperature were also carried out. It was appeared that FS addition contributed to lower bleeding and hydration temperature without disturbance of fresh properties of concrete such as slump and air content compared to non-added concrete. Especially, shrinkage crack resistance of concrete resulted from plastic and drying shrinkage could be effectively reduced by the addition of FS ranging from 1.0% to 1.5%.
본 연구에서는 배합강도 30MPa로 설계된 25-30-18 규격의 콘크리트 배합에 불소화합물 및 실리카로 구성된 불소-실리카 복합형 균열저감제(FS)를 시멘트 중량을 기준으로 0.5% 간격으로 2.0%까지 첨가한 후 슬럼프 경시 변화, 공기량 경시 변화 및 블리딩 등의 굳지 않은 콘크리트의 재료특성을 평가하였다. 또한, 콘크리트 수화온도 변화에 미치는 영향과 소성수축 및 건조수축의 저항성에 미치는 효과를 파악하였다. FS가 첨가된 콘크리트의 재료특성에서 슬럼프 및 공기량 경시 변화는 무첨가 콘크리트에 비해 큰 차이가 없었으나 블리딩과 수화온도는 저감되는 것으로 나타났다. 특히, 경화 전 후 소성수축 및 건조수축에 기인된 콘크리트의 수축균열 저항성이 FS를 $1.0{\sim}1.5%$의 첨가함으로써 크게 저감됨을 알 수 있었다.