Silver Alloying Process for Mokumegane-like Effect for Jewelry Design

장신구 디자인을 위한 모꾸메가네 효과 은 합금 공정

Silver is one of the most appropriate Jewelry materials for Jewelry casting and bench working. The technique known as 'Mokumegane' is good for making silver jewelry with natural patterns, such as wood grain patterns, but the process is not easy for silversmithing because it requires complicated and heavy labour. Instead of using conventional Mokumegane technique, we propose a new modified silver-copper casting process that enables a similar surface effect with good metal bonding strength between silver and copper. Simply pouring the molten silver into pre-aligned copper granules or 0.5 mm to 1.5 mm-thick copper sheets leads to well embedded copper silver ingots. The rolled silver plates from those ingots show excellent bonding interface even after the silver plate rolled ten times. We successfully fabricated prototype rings with copper embedded silver plates. Our result implies that our newly proposed process nay be a simpler way to fabricate silver jewelry with a pseudo-Mokumegane effect.

은은 주조성과 가공성이 뛰어나 장신구 제작에 주된 소재로 채택되어 왔다. 이런 은 소재 자체의 장점을 이용한 전통적인 방법 중 하나인 모꾸메가네는 나뭇결무늬와 같은 자연스러운 금속의 혼합문양을 표현할 수 있어서 부가가치가 높지만 제작 공정이 복잡하고 힘들어서 경제적으로 장신구를 제작하는데 어려움이 있었다. 기존의 모꾸메가네 공정 대신 은과 구리의 융점차를 이용한 변형 주조 방법과 냉간압연으로 구리와 은 두 금속간의 우수한 결합을 유지하면서도 기존의 모꾸메가네와 유사한 표면 장식 효과를 얻을 수 있는 새로운 공정을 제안해 보았다. 직경 3 mm의 구리 그래뉼과 0.5 mm, 1.5 mm 두께의 구리 판재에 순은 용탕을 부어 두 금속간의 확산 접합이 완성된 괴를 만들고, 이후 롤러 압연을 실시하여 두께 1.5 mm의 판재를 만들어서 이를 이용하여 반지 시제품을 제작한 결과, 제안된 공정으로 이종 금속 접합도가 우수하면서 모꾸메가네와 유사한 효과를 성공적으로 낼 수 있었다. 제안된 공정은 기존의 반복된 열간 가공에 의한 복잡한 모꾸메가네 공정에 비해 보다 간단하고 경제적으로 모꾸메가네 효과를 갖는 은 장신구 디자인을 가능하게 함을 확인하였다.