Analysis on Properties of $TiO_2-Nb_2O_5$ Sol

$TiO_2-Nb_2O_5$ 솔의 물성에 대한 분석

  • Published : 2006.07.01

Abstract

[ $TiO_2-Nb_2O_5$ ] sol was prepared using sol-gel method. Crystalline properties of gel powder changed from rutile phase to anatase phase with increasing $Nb_2O_5$ additives at $800^{\circ}C$, while they retained rutile phase regardless of $Nb_2O_5$ additives at $900^{\circ}C,\;1,000^{\circ}C$. They retained amorphous phase from $50^{\circ}C\;to\;400^{\circ}C$, retained anatase phase from $500^{\circ}C\;to\;600^{\circ}C$ and had rutile phase over $700^{\circ}C$ at 1mole% $Nb_2O_5$ additive. After $TiO_2-Nb_2O_5$ sol retained low viscosity with normal chain structure for a long time, its viscosity increased fast with network structure. DTA properties of gel powder had endothermic reaction due to evaporation of propanol and water about $78^{\circ}C$, had exothermic reaction due to propanol combustion about $290^{\circ}C$ and had exothermic reaction due to changing of $TiO_2$ phase about $640^{\circ}C$.

Keywords

References

  1. L. L. Hench, in Ultrastructure Processing of Ceramics, Glasses and Composites, Wiley, New York, pp.3-5, 1984
  2. 안화승,'나노기술과 소재',인하대학교 출판부,p.47-53, 2004
  3. P. Y. Simons and F. Dachille, Acta Cryst., 23, pp. 334-336, 1967 https://doi.org/10.1107/S0365110X67002713
  4. A. Navrosky, J. C. Jamieson and O. J. Kleppa, Science, 158, pp.338-339, 1967 https://doi.org/10.1126/science.158.3799.388
  5. A. von Hippel, 'Dielectric Materials and Application', Artech House, pp.3-46, 1995
  6. C. C. Wand, K. H. Zaininger and M. T. Duffy, RCA Rev., 31, p.728, 1970
  7. S. Hishita, M. Takata and H. Yanagida, 'Inhibition of Anatase-Rutile Transformation due to Nb2O5 Addition', Journal of the Ceramic Society of Japan, 86, pp.631-632, 1978 https://doi.org/10.2109/jcersj1950.86.1000_631
  8. K. Katayama, T. Akiba, G. Sudoh, M. Takata and H. Yanagida, 'Effect of Addition of Nb2O5 on Sintering and Electrical Conductivity of Rutile', Funtai-oyobi-Funmatsu-Yaki, 29, pp.146-150, 1982