Conservation for Wooden Objects Excavated From Imdang, KyungSan - Wooden frame of Armor and Lacquer Wares -

경산 임당유적 목제품 보존 - 갑옷틀 및 칠기 -

The wooden armor frame and various lacquerware artifacts excavated from the low swamp remains in Imdang, Gyeongsan have very weak material and lacquer coating; in case they are exposed in the air, they are likely to be shrunken and deformed immediately. The wooden armor frame has large size and it might be dissolved during freeze-drying. The lacquer coating of lacquerware blocks the penetration of chemicals and it is very likely to swell or peel off during the treatment. Therefore, to prevent the dissolution during vacuum freeze-drying, the wooden armor frame was replaced with t-butanol and impregnated in t-butanol solution with PEG#3, 350 43%, and lacquerware was impregnated in PEG#3, 350 40% solution at room temperature and freeze-dried. According to the analysis of the lacquer fragment from the lacquerware, the lid and the mounted cup was pasted with the mixture of lacquer and black pigment (soot) on the base layer after the first coating and pasted two or three times more with natural lacquer; the red lacquered wooden cup was pasted with the mixture of lacquer and black pigment on the base layer and pasted once on the middle layer. The top lacquer (red) was pasted with the mixture of iron oxide(Fe₂O₃).

경산 임당저습지유적에서 출토된 목제 갑옷틀과 다양한 칠기유물들은 재질이 매우 취약하고 옻칠이 되어 있어 공기 중에 노출되면 건조가 진행되어 곧바로 수축·변형이 일어나기 쉽다. 목제 갑옷틀의 경우 대형으로 동결건조과정 중 융해의 발생우려가 있고 칠기의 경우 목재표면에 옻칠이 되어있어 약제가 잘 침투되지 않고 처리 중 칠막이 부풀거나 탈락될 우려가 높다. 따라서 목제 갑옷틀은 진공 동결건조과정 중 융해방지를 위하여 t-butanol로 치환한 후 최종 PEG#3,350 43%의 t-butanol용액에 함침하고, 칠기는 최종 PEG#3,350 40%의 수용액(水溶液)에 실온에서 함침처리 후 동결 건조하여 보존처리 하였다. 칠기의 칠 도막 분석결과 뚜껑 및 고배는 초칠을 한 후 밑층에 흑색안료(그을음)와 옻칠을 혼합하여 바른 후 2-3회 생칠을 하였고 주칠 컵형목기는 밑층에 흑색안료와 옻칠을 혼합하여 바른 후 그 위에 1회 중칠을 하였으며, 산화철(Fe₂O₃: 석간주)이 붉은 칠의 발색안료로 쓰였을 가능성을 보여준다.