Corrosion Resistance of Cr-bearing Rebar to Macrocell Corrosion Caused by Concrete with Crack

피복 콘크리트의 균열 발생에 기인한 매크로셀 부식 환경하에서의 Cr강방식철근의 방식성

  • 태성호 (한양대학교 친환경건축 기술혁신 연구센터)
  • Received : 2005.08.09
  • Published : 2006.07.30
Download PDF
⟨ Previous Next ⟩

Abstract

This study was investigated to corrosion resistance of Cr-bearing rebars to macrocell corrosion caused by concrete with crack. Ten types of steel bars having different Cr contents were embedded in concretes with imitation crack. The corrosion resistance of the Cr-bearing rebar was examined by measuring half-cell potential, macrocell corrosion current, corrosion area and weight loss up to 105 cycles of salt spray testing. The results revealed that the Cr content required for corrosion resistance in a macrocell corrosion environment caused by chloride ion gap of $3kg/m^3$ was 9% or more. The corrosion-resisting performance of Cr-bearing rebar was particularly noticeable with a Cr content of 11% or more.

피복 콘크리트의 균열 발생에 기인한 매크로셀 부식 환경하에서의 Cr강방식철근의 방식성을 평가하기 위하여 10종류의 Cr강방식철근을 콘크리트에 매입 후 피복 콘크리트에 모사 균열을 발생시킨 공시체를 제작하였다. 그 후 염수 분무 촉진 양생 105사이클까지의 매크로셀 부식전류밀도의 경시변화와 아노드 캐소드 철근의 자연전위, 부식면적률, 부식감량률을 측정함으로써 Cr강방식철근의 방식성에 대하여 검토하였다. 그 결과, 염화물 이온 농도차 $3kg/m^3$ 이하의 매크로셀 부식 환경에 대하여 Cr함유율 9% 이상의 Cr강재에서 방식성이 확인되었으며 특히, Cr함유율 11% 이상의 Cr강재에서 뛰어난 방식성이 입증되었다.

Keywords

References

  1. 青木　繁, "境界要素法による腐食防食問題の解析,"裳華房, 1998, p.5.
  2. 宮里心一, "鉄筋コンクリートの欠陥部に生じる塩害および中性化によるマクロセル腐食に関する研究," 東京工業大学博士学位論文, 2001.
  3. 片脇清士, "最新のコンクリート防食と補修技術," 山海堂, 2000, pp.48-53.
  4. 腐食防食協会, "金属の腐食.防食Q＆A 電気化学入門編," 丸善株式会社, 2002, pp.10-11.
  5. 日本規格協会, "塩水噴霧試験方法," JIS Z 2371, 2000, pp.1-48.
  6. 日本規格協会, "硬化コンクリート中に含まれる塩化物イオンの試験方法," JIS A 1154, 2003, pp.1-18.
  7. 日本コンクリート協会, "コンクリート構造物の腐食.防食に関する試験方法ならびに基準（案）, JCI-SCI コンクリート中の鋼材の腐食評価方法," 1987, pp.1-2.
  8. McDonald, D. B., "Stainless Steel Reinforcing as Corrosion Protection," Concrete International, May 1995, pp.65-70.
  9. Sung-Ho Tae, "Corrosion Behaviorof Cr-bearing Corrosion Resistant Rebar in Concrete with Chloride Ion Content," Journal of the Architectural Institute of Korea, Vol. 7, NO. 1, 2005, pp.49-54.
  10. Lopez, W., Gonzales, J. A., "Influence of the degree of pore saturation on the resistivity of concrete and the corrosion rate of steel reinforcement," Cement and Concrete Research, Vol.23, 1993, pp.368-376. https://doi.org/10.1016/0008-8846(93)90102-F
  11. Okamoto, G., "Proc.5th Int. cong. on Metallic Corrosion," 1972, p.8.