Abstract
In this sturdy, spherical activated carbon(SPAC) contained $TiO_2$ was made by ion-exchanged treatment and heat treatment for applying fluidizing bed system. The ion-exchange resin was treated by $TiCl_3$ aqueous solution. The treated resin and raw resin were heat-treated under nitrogen condition to convert into Ti-SPAC. During the heat-treatment, burn-off weight amounts and the element were measured by means of TGA and TGA/MS, individually. The physicochemical properties of Ti-SPAC was characterized by means of XRD, SEM, EDS, BET, EPMA, ESR, intensity and titanium content. The Ti-SPAC had spherical shape with diameter size about $350{\mu}m{\sim}400{\mu}m$ and $617m^2/g$ specific surface area. Structure of $TiO_2$ in Ti-SPAC was anatase and rutile form. Also, $TiO_2$ on SPAC were found that the $TiO_2$ were uniformly distributed through EPMA analysis. Moreover, the Ti-SPAC showed indirect photocatalyst activity estimation through ESR analysis, characteristics of photocatalyst potentially. Over all results, Ti-SPAC was used in fluidizing bed UV/photocatalyst system to remove HA(Humic Acid). That results were HA removal efficiency was about 70% and Ti-SPAC intensity was preserved during reaction. Ti-SPAC showed practical possibility as photocatalyst in fluidizing bed system.
티타늄 담지 구형활성탄(spherical activated carbon, SPAC)을 제조하여 유동상 광촉매 반응에 적용하고 그 특성을 평가하였다. 티타늄을 담지하기 위하여 염화티타늄용액으로 이온교환 처리된 이온교환수지를 열처리 과정을 통하여 구형활성탄으로 변환시켜 주었다. 열처리 과정 중 감량되는 성분 및 무게 변화는 TGA/MS 분석을 통하여 알아보았으며,Ti을 함유한 구형활성탄의 물리화학적 성질은 SEM, XRD, EPMA, ESR, EDS, BET와 같은 분석을 통하여 그 특성을 알아보았다. 그 결과 Ti-구형활성탄의 입자 크기는 $350{\mu}m{\sim}400{\mu}m$, 비표면적은 $617m^2/g$ 이였으며, 담지 된 티타늄은 $TiO_2$ anatase 형태와 rutile 형태가 주를 이루고 있음을 알 수 있었다. 구형활성탄에 담지 된 $TiO_2$는 약 6 wt%로 균일한 분산도로 구형활성탄 표면에 담지 된 것을 EPMA 분석을 통해 알 수 있었다. 더욱이 ESR 분석을 통하여 간접적인 광촉매 활성을 확인할 수 있었으며, 따라서 이러한 결과들을 바탕으로 유동상 광반응조를 이용한 HA(humic acid) 광분해 반응에 적용하였다. 그 결과, 제거 효율이 약 70% 정도로 높게 나타났을 뿐만 아니라 반응 중에도 Ti-구형활성탄의 강도가 계속 유지되어 유동상 반응에서의 광분해 촉매로서 활용가능성을 보여주었다.