Studies on Evaluation for Long-Term Structural Performance of Pinus densiflora Sieb. et Zucc. (I) -Shear Creep and Mechano-Sorptive Behavior of Drift Pin Jointed Lumber-
Hong, Soon-Il
(Department of Wood Science & Engineering, College of Forest Science, Kangwon National University)
;
Park, Jun-Chul
(Department of Wood Science & Engineering, College of Forest Science, Kangwon National University)
This study was carried out to evaluate the mechano-sorptive deflection of shear creep of drift pin jointed solid wood. Specimens were the solid wood of Pinus densiflora. The joint was composed with steel plate and drift pin, 85mm in length and 10mm in diameter. The creep tests were conducted under the constant loads in an variable environment. Five different shearing loads were applied parallel to the grain of specimens. The shearing loads applied were 170, 340, 510, 680 and 850 kgf. The stress levels were 10, 20, and 30, 40 and 50% of the bearing strength obtained from the tension-type lateral strength test. The creep tests for specimens were carried out for 10300 hours. A few general conclusions could be drawn from this study: The mechano-sorptive deflection (${\delta}$ ms) is defined as ${\delta}\;ms={\delta}\;t-({\delta}\;c+{\delta}\;sh)-{\delta}\;o$, where ${\delta}$ t is the total deflection, ${\delta}$ c is the pure creep, ${\delta}$ sh is shrinkage-swelling behavior, and ${\delta}$ o is the initial deflection. Changes of relative humidity may cause more severe creep deflection than those of constant humidity, especially during the drying process. The mechano-sorptive behaviors of specimens, except the effects of shrinkage and swelling, gradually increased with increasing time. The deflection is increased in desorption process and recovered in adsorption process. The deflections of drift pin jointed solid wood under different loads showed almost same tendency in all specimens. Although the creep deflection tendencies of each series are very similar, the specimens subjected to a large shearing load exhibit large creep deflections in the desorption process than do those to the small shearing load specimens.
Hoyle, R. J., R. Y. Itani, and J. J. Eckard. 1986. Creep of douglas fir beams due to cyclic humidity fluctuations. Wood fiber Sci. 18(3): 468-477
Ranta-Maunus, A. 1975. The viscoelasticity of wood at varying moisture content. Wood Sci. Tech. 9(3): 188-206https://doi.org/10.1021/es60101a902
Ranta-Maunus, A. 1991. The effect of naturally changing humidity on the creep of timber structure. International Timber Engineering Conference, London. 4,172-4,179
Rouger, F. 1990. Creep behavior of trench wood. International Timber Engineering Conference, Tokyo. 330-336
Sabo, T. and G. Ifju. 1970. Influence of stress on creep and moisture distribution in wooden beams under sorption condition. Wood Sci. 2(3): 159-167
Toratti, T. 1991. Study on the existence of a rnechano-sorptive creep limit considering available test result. Wood mechanics workwhop on fundamental aspects on the creep of wood, Lund, Sweden
Van der Put, T. A. C. M. 1989. Theoretical explanations of the mechano-sorptive effect in wood. Wood fiber Sci. 21(3): 219-230
Hong, S. I. and A. Taranori. 1993. Creep of nail plate jointed glulams and solid glulams under changing humidity. Mokuzai Gakkishi. 39(9): 1,020-1,026