Formation of (TEACOOH)-Montmorillonite Intercalations Complex and Polycondensation between the Layers of the Complex

(TEACOOH)-Montmorillonite 층간화합물의 형성 및 층 내에서의 고분자화 반응

[TEACOOH]-Montmorillonite intercalations complex obtained from Na-Montmorillonite and 10-Carboxy-n-decyldimethylethylammonium bromide(organic cation) was reacted with the monomer($\varepsilon$-caprolactone) to achieve the [TEACOOH]-$\varepsilon$-caprolactone-Montmorillonite intercalations complex. From intercalations complex Montmorillonite/Polycaprolactone Nanocomposite in which montmorillonite(inorganic material) is chemically linked with the polycaprolactone(organic polymer) was formed at $220^{\circ}C$ for 48 h. The basal spacing for the sample obtained after polymerization, extraction with methanol and dried at $65^{\circ}C$ in high vacuum for 24 h was 50.7 $\AA$.

Na-Montmorillonite와 10-Carboxy-n-decyltriethylammonium bromide (유기 양이온) 사이의 양이온 교환반응에 의해 얻어진 [TEACOOH]-Montmorillonite 층간화합물을 유기 단분자인 $\varepsilon$-caprolactone을 반응시켜 [TEACOOH]-$\varepsilon$-caprolactone-Montmorillonite 층간화합물을 형성하였다. 이렇게 얻어진 [TEACOOH]-$\varepsilon$-caprolactone-Montmorillonite 층간화합물을 $220^{\circ}C$의 온도 하에서 48시간 동안 가열하여 고분자화시켜 무기물질인 몬모릴로나이트와 유기 고분자인 폴리카프로락톤이 화학적으로 결합된 몬모릴로나이트/폴리카프로락톤 나노복합재료를 제조하였다. 고분자화반응을 수행한 후 얻어진 시료를 메탄올을 이용하여 추출한 뒤 고진공 하에 $65^{\circ}C$로 24 시간 동안 건조시킨 후에 얻은 층간거리 값으로는 34.24 $\AA$이 얻어졌다.