Abstract
This paper was to evaluate the high strength lightweight self-compacting concrete(HLSCC) manufactured by Nan-Su, which main factor, Packing Factor(PF) for mixing design, has been modified and improved. We have examined HLSCC performance at its fresh condition as well as its mechanical properties at the hardened condition. The evaluation of HLSCC fluidity has been conducted per the standard of second class rating of JSCE, by three categories of flowability(slump-flow), segregation resistance ability(time required to reach 500mm of slump-flow and time required to flow through V-funnel) and filling ability(U-box test) of fresh concrete. The compressive strength of HLSSC at 28 days has come out to more than 30MPa in all mixes. The relationship between the compressive strength-splitting tensile strength and compressive strength-modulus of elasticity of HLSSC were similar those of typical lightweight concrete. Compressive strength and dry density of HLSCC at 28 days from the multiple regression analysis resulted as $f_c=-0.16LC-0.008LS+50.05(R=0.83)\;and\;f_d=-3.598LC-2.244LS+2,310(R=0.99)$, respectively.
본 연구에서는 Nan-Su의 자기충전콘크리트(Self-Compacting Concrete)의 배합설계 방법중 주요인자인 골재 채움률(Packing Factor : PF)을 수정 및 보완한 배합설계 방법을 이용하여 고강도경량 자기충전콘크리트(High Strength Lightweight Self-Compacting Concrete)를 제조하고 자기충전성 및 역학적 특성을 검토하였다. 콘크리트의 자기충전성 평가는 Slump-flow, V-funnel 유하시간, Slump-flow mm도달시간 및 U-box 충전높이를 측정하여 일본토목학회(JSCE)의 자기충전콘크리트 기준 중 2등급 범위를 적용시켜 검토하였다. 고강도경량 자기충전콘크리트의 재령 뽀일 압축강도는 모든 배합에서 30MPa 이상으로 나타났으며, 압축강도와 쪼갬 인장강도 및 탄성계수의 비는 기존의 연구경향과 유사한 값을 나타내고 있었다 또한, 재령 28일 압축강도와 기건 단위용적질량은 다중회귀분석 결과 $f_c=-0.16LC-0.008LS+50.05(R=0.83)$ 및 $f_d=-3.598LC-2.244LS+2,310(R=0.99)$로 나타났다.