A Study on the Friction and Wear Characteristics with Purity on $AL_{2}O_{3}$ Ceramic

$AL_{2}O_{3}$ 세라믹의 순도에 따른 마찰 마모 특성 연구

The tribological properties of ceramics are very important in the application to engineering ceramic parts such as seal rings, pump parts, meter parts, and so on. In this study, the effects of each other purity on the mechanical and tribological properties of alumina and zirconia ceramics were investigated. Sliding distance, sliding speed, contact load. friction coefficient, the amount of worn out material at a certain time, and the prepared composites were measured. Crystalline phases and microstructure were examined with XRD and SEM. We obtained the good properties of friction coefficient and wear resistance at the purity 99.7$\%$ of alumina. However, The purity 95$\%$ were great at the wear amount of worn out material.

세라믹을 실링, 펌프부품, 미터계 부품 등에 이용할 때 마찰마모 특성은 매우 중요하다. 본 연구에서는 알루미나를 기계적 및 마찰마모의 특성에 미치는 영향을 고찰 하였다. 미끄럼거리와 미끄럼 속도, 그리고 마모량과 마찰계수 등을 서로 다른 순도에 따라 측정하고, 결정상 분석과 미세구조는 각각 XRD와 SEM으로 조사하였다. 알루미나의 순도 95$\%$가 상대적으로 마모량이 가장 크고, 순도 99.7$\%$가 마찰계수와 마찰마모 저항성이 우수하였다.