Effect of Die Machining Method on the Surface of Die Steel STD11

금형가공방법이 합금공구강 표면에 미치는 영향

This paper has comparatively analyzed the characteristics of the machined surface of a specimen made by machining Die Steel STD11 and a specimen obtained by W-EDM steel. If a press die is manufactured through W-EDM, products of shapes that cannot easily be made through machining can be manufactured easily. However, the life of the press die is significantly reduced compared with the press die made through machining. This is believed to be caused by the deformed layer that has occurred on the surface of the press die that was made through W-EDM. The roughness of the 2 specimens was measured, and it was learned that the distribution of the roughness of the specimen made through the 1st W-EDM was rough. When the specimens were observed using a scanning-electron microscope, there was significant difference between the surface and the cross-section of the 2 specimens, while the cross section of the specimen obtained through W-EDM had the tempered and quenched surface structure which exists in the form of a deformed layer.

본 논문은 합금공구강을 기계 가공한 시편과 와이어 컷 방전가공한 시편의 가공면 표면 특성을 비교 분석한 것이다. 와이어 컷 방전가공으로 금형을 제작하면 기계가공으로 가공하기 어려운 형상의 제품을 쉽게 제작할 수 있다. 그러나 기계가공으로 제작된 금형에 비해 수명이 현저히 저하된다. 이러한 요인은 와이어 컷 방전가공으로 제작 된 금형 표면에 가공 변질층이 발생하기 때문이라 사료된다. 두 시편의 표면 거칠기 측정 결과 1차 와이어 컷 방전가공한 시편의 표면 거칠기 분포가 거칠음을 알 수 있었다. 주사 전자 현미경 관찰 결과 두 시편의 표면부와 단면부는 큰 차이를 보였고 와이어 컷 방전가공한 시편의 단면부는 표면의 급열 급랭된 조직이 가공 변질층으로 존재함을 알 수 있었다.