Abstract
The objective of this study was to determine the effect of extrusion temperature on puffing of white and red ginseng powder. The extrusion variables were feed material (red and white ginseng powder) and die temperature $(100\;and\;115^{\circ}C)$. The analyzed characteristics of ginseng extrudates were sectional expansion index, microstructure and rheological properties. Most of biopolymer was highly puffed at higher extrusion temperature, but the cross-sectional expansion of white and red ginseng powder was higher at 1000e and longitudinal expansion seems to higher at $115^{\circ}C$. White and red ginseng powder were puffed inconsistently and discontinuously at $115^{\circ}C$. The scanning electron microphotograph of extruded white ginseng was uniform air cell distribution at 100oe, but pore size increased at $115^{\circ}C$ and had fine uniformity due to pore explosion. White ginseng and its extrudate were pseudoplastic. Intrinsic viscosity was lower as a result of increased die temperature. The cross-sectional expansion seems to be inconsistent and decreased due to decrease in melt viscosity at $115^{\circ}C$.
압출성형 온도에 따른 백삼과 홍삼분말의 팽화현상을 살펴보기 위해 팽화율, 미세구조 및 유동특성을 분석하였다. 압출성 형 공정 변수는 원료(백삼과 홍삼가루)와 사출구 부위온도($100^{\circ}C$ 와 $115^{\circ}C$)로 설정하였다. 사출구 부위온도가 $120^{\circ}C$ 이상의 고온에서 잘 팽화되지만, 백삼분말과 홍삼분말은$100^{\circ}C$에서 사출구 직경방향으로 팽화율이 높았으나 $115^{\circ}C$로 증가와 함께 사출구 직경방향 팽화율은 감소하였으나 가로 방향으로 팽화율이 증가하여 비연속적인 팽화가 일어나 압출성형물 표면은 기공의 파열에 거칠었다. 또한 백삼 압출물의 미세구조는 사출구 온도$100^{\circ}C$에서 기공이 작고 균일하였지만 $115^{\circ}C$로 증가와 함께 기공의 파열에 의해 기공의 크기가 불균일하고 크기도 증가한 것을 관찰하였다. 백삼분말과 압출성형 백삼분말은 의가소성유체였으며 고유점도는 사출구 부위온도가 증가함에 따라 감소하여 사출구 부위온도의 증가와 함께 백삼전분의 구조가 파괴되어 분자량이 감소하는 것으로 판단되었다. 분자량의 감소와 함께 용융반죽의 점도가 낮아져 압출성형 온도 $115^{\circ}C$에서 직경 팽화율의 감소와 함께 불연속적인 팽화가 일어난 것으로 판단되었다.