Effect of Alumina contents in Feldspar and cullet for the Soda-lime glass manufacturing

Soda-Lime Glass에서 Cullet과 장석의 첨가에 따른 Alumina 변화가 제조공정에 미치는 영향

The first aim of mass product of glass in Automatic bottle glass industry is to decrease the cost and to increase the quality. Second, the cullet is how widely used to save the energy and reducing of ecomaterials. However the physical and chemical properties of Soda-lime glass would be come true at the lower than 2% $Al_2 O_3$. Unfortunately the $Al_2 O_3$ contents of domestic silica is greater than 4% Since small glass class than 200ml bottle is made in domestic silica the producting efficiency would be decreased due to the defect such as cord, knot, devitrite, pore etc. There are many problems such as devitrifiacation and deteriorated effect on production in glass industry became of increasing of plate glass cullet. It is tried to solve these kinds of problems using various analysing methods in this experiments.

현재 유리병의 대량생산을 목적으로 하는 자동 제병공장에서는 저렴하면서도 질 좋은 유리를 생산하고자 하는 것이 첫째 목적이다. 이 목적에 가장 경제적으로 접근하면서 수입 원료에 비하여 훨씬 저렴한 국내산 원료의 효율적인 활용방안의 연구와 에너지절감 및 환경 친화적인 자원재활용 등을 목적으로 파유리를 사용하고 그 양을 늘리기를 원하고 있다. 그러나 소다석회유리에서 $Al_2 O_3$의 함량이 2%미만일 때는 물리화학적인 장점이 실현될 수 있으나, 국내에서는 이러한 좋은 규사를 채광 할 수 없고, 채광 가능한 제품은 $Al_2 O_3$의 함량이 4%이상이므로 국내산 규사만으로 유리조성의 $Al_2 O_3$의 함량을 2%미만으로 조절하기는 불가능한 실정이다. 따라서 낮은 품질의 유리물로서 생산이 가능한 200ml 이하의 소형 유리병(특히 갈색약품 병) 생산 공장에서는 국내산 규사만을 사용하여 유리물을 만들고 있으나, $Al_2 O_3$함량증가에 따라 발생되는 결점(Cord, Knot, 실투, 기포 등)의 증가로 생산효율이 크게 떨어지고 있다. 또한 파유리 투입 시 병유리와는 조성상의 이질성에서 오는 결점의 발생과 파유리 사용량의 증가에 따른 유리물점도 상승으로 용해로 바닥의 온도가 낮은 유리물 정체부위의 실투발생 등 생산 공정에 나쁜 영향을 미치는 여러 가지 문제점들이 발생하게 되었다. 실험을 통해 얻은 결과를 여러 가지 분석 방법을 통해 관찰, 분석하여 이러한 문제점을 해결하였다.