Characteristics of Electrical Resistance in System Mn-Co-Ni-Fe oxide for Thermistor with various Compositions

서미스터용 Mn-Co-Ni-Fe계 산화물의 조성에 따른 전기저항특성

  • Kim, Yeong-Min (Dept. of Mat'ls Eng., Col of Eng., Chungbuk National University) ;
  • Im, Jae-Seok (Dept. of Chem. Eng., Col of Eng., Inha University) ;
  • Im, Goeng (Dept. of Adv. Mat'ls Eng., Paichai University)
  • 김영민 (충북대학교 공과대학 재료공학과) ;
  • 임재석 (인하대학교 공과대학 화학공학과) ;
  • 임굉 (배재대학교 공과대학 신소재공학부)
  • Published : 2004.01.20

Abstract

The properties of electrical resistance of Mn-Co-Ni-Fe oxide-based thermistor with various Fe contents in sintering process at $1200^{\circ}$ to $1400^{\circ}C$ for 4 hours in air atmosphere for fabricating thermistor materials were investigated. The results were as follows: all samples showed single cubic spinel crystal structures in all region. The electrical conductivity is the highest thermistor sintered at $1300^{\circ}C$ for 4 hours. In general when the Fe content is increased except F-2, the resistivity increases and relatively the conductivity decreases. Particularly F-2 composition exhibited the highest electrical conductivity (1.4${\times}$$10^-3$${\textohm}cm) and relatively low B constant(2906K)

Mn-Co-Ni 3성분계에 Fe의 첨가량을 변화시켜 따른 산화물 서미스터소결체(Mn-Co-Ni-Fe oxide)를 소성온도 1200~$1400^{\circ}C$에서 제조하여 전기저항특성을 조사한 결과, 결정상은 단일입방정 스피넬형 결정구조였고, 소성온도에 따른 전기전도도는 $1300^{\circ}C$에서 4시간 소결한 시미스터가 가장 높았다. 대체로 F-2를 제외하고는 Fe의 첨가량이 증가할 때 비저항은 증가하고 상대적으로 전기전도도는 감소한다. 특히 F-2의 조성에 있어서는 전기전도도가 1.4${\times}$$10^-3$${\ textohm}cm로 높았고 상대적으로 B정수는 2906K로 낮았다.