Effect of Low Pressure Steam Explosion Treatment on Prevention of Resin Exudation from Wood under High Temperature Surroundings

저압증기폭쇄(低壓蒸氣爆碎)처리가 고온영역(高溫領域)하에서의 목재(木材) 수지삼출(樹脂渗出) 예방에 미치는 영향

This study was carried out to find the efficient methods for preventing resin exudation from spruce board during high temperature environment service.In the dry-air oven test, in-use temperature related to resin exudation of 110℃ could be obtained by the appropriate kiln drying without any special treatment, and the in-use temperature of the radio-frequency/vacuum (RF/V)-dried boards was about 20℃ higher than that of the conventional kiln-dried boards.In the autoclave test, resin exudation was not found from any board dried in the conventional kiln and in the RF/V kiln after the low pressure steam explosion (SE) treating, while for the control resin exudations were more severe in the autoclave test above 130℃ than in the dry-air oven test. It, therefore, would be suggested that resin exudation during high temperature service condition can be prevented more effectively by super-heated steaming green boards than by high-temperature drying boards with low moisture.

본 과제는 Spruce재가 사우나와 같은 고온 공간용 부재(部材)로 사용되어질 때 나타나는 수지삼출의 문제점을 해결하여 그 방안을 제시코저 수행하였다. 건식(乾式)공간용 부재(部材)의 경우 적절한 열기건조가 이루어진다면 별도의 처리를 실시하지 않더라도 110℃의 수지삼출 안정선을 얻을 수 있는 것으로 확인되었으며, 고주파진공건조에 의해 수지삼출 안정선이 열기건조보다 약 20℃ 정도 더 상승하였다. 습식(濕式)폭로시험에서는 저압증기폭쇄처리재의 경우 열기건조재나 고주파진공건조재 모두 수지가 전혀 삼출되지 않은 반면에, 무처리재의 경우 건조방법에 관계없이 130℃ 이상의 폭로조건에서는 수지삼출의 정도가 건식(乾式)폭로시험의 경우보다 심한 것으로 나타나, 수지삼출을 예방하기 위하여 인공건조중 저(低)함수율 상태의 건조말기에 고온(高溫)을 적용하여 건조하는 것보다는 건조전 고(高)함수율 상태에서 과열(過熱)증기로 분무(噴霧)처리하는 것이 더 바람직한 것으로 확인되었다.