Journal of the Korean Wood Science and Technology
- Volume 32 Issue 3
- /
- Pages.8-14
- /
- 2004
- /
- 1017-0715(pISSN)
- /
- 2233-7180(eISSN)
Nondestructive bending Strength Evaluation of Woodceramics Using Resonance Frequency Mode (I) - Carbonizing Temperature -
- Byeon, Hee-Seop (Faculty of Forest Science, Institute of Agriculture & Life Science, Gyeongsang Nat'l Univ.) ;
- Ahn, Sang-Yeol (Faculty of Forest Science, Institute of Agriculture & Life Science, Gyeongsang Nat'l Univ.) ;
- Oh, Seung-Won (Faculty of Forest Science, Chonbuk Nat'l Univ.) ;
- Piao, Jin-Ji (Faculty of Forest Science, Chonbuk Nat'l Univ.)
- Received : 2003.05.10
- Accepted : 2003.07.10
- Published : 2004.05.25
Abstract
Nondestructive evaluation (NDE) technique method using a resonance frequency mode was carried out for woodceramics produced at different carbonizing temperatures (600℃, 800℃, 1000℃, 1200℃, 1500℃) at the phenol resin impregnation rate of 70%, for three kinds of species (Pinus densifora, Pinus koraiensis, Larix leptolepis), respectively. There was a poor relationship between density and static bending MOR. However, close correlations were found between dynamic MOEd and static bending MOR, and between static MOEs and MOR. Especially, the correlation coefficient was highest between MOEd and static bending MOR. Therefore, the MOEd using the resonance frequency mode is useful as a NDE method for predicting the MOR of woodceramics produced at different carbonizing temperatures.