Synthesis and Properties of Photocurable Epoxy Modified Acrylates Using Half-Ester Acrylates

하프-에스터 아크릴레이트를 이용한 광경화형 에폭시 변성 아크렐레이트의 합성과 물성

  • 김동국 (한양대학교 신소재화학과) ;
  • 임진규 (한양대학교 신소재화학과) ;
  • 김우근 (한양대학교 신소재화학과) ;
  • 허정림 (건국대학교 신소재공학과)
  • Published : 2004.11.01
Download PDF
⟨ Previous Next ⟩

Abstract

Various half-ester acrylates were prepared from anhydrides and 2-hydroxyethyl acrylate. Photocurable epoxy modified acrylates were prepared from synthesized half-ester acrylate and neopentylglycol diglycidylether. Physical properties such as hardness, yellowing, tensile strength and elongation were tested and compared as the structure of oligomer in cured-film differs. It was found that viscosity of neopentylglycol diglycidylether-hexahydrophthalic anhydride (NP-HA) was highest. Hardness and tensile strength of photocrosslinked neopentylglycol diglycidylether-hexahydrophthalic anhydride were better than those of other photocrosslinted epoxy acrylates. And 5% weight loss temperature of photocrosslinked neopentylglycol diglycidylether-hexahydrophthalic anhydride was higher than those of other photocrosslinked epoxy acrylates. Value of yellow index of photocrosslinked neopentylglycol diglycidyl ether-succinic anhydride (NP-SA) was lower than the other products.

다양한 하프-에스터 아크릴레이트를 합성하기 위하여 다양한 산 무수물에 2-하이드록시에틸 아크릴레이트 (2-hydroxyethyl acrylate)를 반응시켰다. 합성된 하프-에스터 아크릴레이트에 지방족 에폭시 화합물인 네오펜틸글리콜 디글리시딜에테르 (neopentylglycol diglycidylether)를 반응시켜 광경화형 에폭시 변성 아크릴레이트를 제조하였다. 점도는 헥사하이드로프탈산 무수물 (hexahydrophthalic anhydride)을 사용하여 반응시킨 네오펜틸글리콜 디글리시딜에테르-헥사하이드로프탈산 무수물 (NP-HA)이 가장 높았다. 또한 헥사하이드로프탈산 무수물을 사용한 네오펜틸글리콜 디글리시딜에테르-헥사하이드로프탈산 무수물의 광경화물은 비교적 다른 산 무수물을 사용하여 제조한 에폭시 변성 아크릴레이트의 광경화물보다 경도, 인장 강도가 우수하였으며, 5% 무게 감소 온도도 높은 것으로 보아 열적으로 안정하다는 것을 알 수 있었다. 황변 지수값은 숙신산 무수물 (succinic anhydride)을 사용하여 반응시킨 네오펜틸글리콜 디글리시딜에테르-숙신산 무수물 (NP-SA)이 가장 낮았다.

Keywords

References

  1. M. Braithwaite, S. Davidson, R. Holman, C. Lowe, P. K. T. Oldring, M. S. Salim, and C. Wall, 'Chemistry & Technology of UV & EB Formulation for Coatings, Inks & Paints', P. K. T. Oldring, Editor, SITA Technology, London, 1991
  2. S. P. Pappas, 'Radiation Curing', Plenum, New York, 1992
  3. S. P. Pappas, 'UV Curing: Science and Technology', Technology Marketing Corporation, Connecticut, 1983
  4. J. C. Jung, Polymer(Korea), 10, 570 (1986)
  5. C. E. Hoyle and J. F. Kinstle, 'Radiation Curing of Polymeric Materials', American Chemical Society, Washigton DC, 1990
  6. G. Orcel, S. Vanpoulle, J. Y. Barraud, J. Y. Boniort, and B. Overton, Wire, 46, 206 (1996)
  7. A. H. Rodas, R. E. S. Bretas, and A. Reggianni, J. Mater. Sci., 21, 3025 (1986)
  8. S. B. Lin, S. Y. Tsay, T. A. Spechhard, K. K. S. Hwang, J. J. Jezerc, and S. L. Cooper, Chem. Eng. Commun., 30, 251 (1984)
  9. T. A. Speckhard, K. K. S. Hwang, S. B. Lin, S. Y. Tsay, M. Koshiba, Y. S. Ding, and S. L. Cooper, J. Appl. Polym. Sci., 30, 647 (1985)
  10. M. A. Ali, M. A. Khan, and K. M. I. Ali, J. Appl. Polym. Sci., 60, 879 (1996)
  11. J. W. Yoo and D. S. Kim, Polymer(Korea), 23, 376 (1999)
  12. H. D. Kim, D. J. Lee, J. H. Choi, and C. C. Park, Polymer(Korea), 18, 38 (1994)
  13. K. H. Lee and B. K. Kim, Korea Polym. J., 4,1 (1996)
  14. H. D. Kim, S. G. Kang, and C. S. Ha, J. Appl. Polym. Sci., 46, 1339 (1992)
  15. Y. Otsubo, T. Amari, and K. Watanabe, J. Appl. Polym. Sci., 29, 4071 (1984)
  16. T. Matynia, R. Kutyla, K. Bukat, and B. Pienkowska, J. Appl. Polym. Sci., 55, 1583 (1995)
  17. M. Bajpai, V. Shukla, and A. Kumar, Progress in Organic Coatings, 44, 271 (2002)
  18. T. Maruno, S. Ishibashi, and K. Nakamura, J. Polym. Sci.; Part A: Polym. Chem., 32, 3211 (1994)
  19. W. Shi and B. Ranby, J. Appl. Polym. Sci., 51, 1129 (1994)
  20. T. R. Williams, J. Appl. Polym. Sci., 31, 1293 (1986)
  21. R. Bongiovanni, G. Malucelli, M. Sangermano, and A. Priola, Progress in Organic Coatings, 36, 70 (1999)
  22. J. K. Lim, D. K. Kim, and J. Y. Hwang, J. Korean Ind. Eng. Chem., 14, 6 (2003)
  23. J. K. Lim, D. K. Kim, and W. G. Kim, J. Korean Ind. Eng. Chem., 15, 225 (2004)
  24. Y. C. Kim and B. J. Lee, J. Korean Ind. Eng. Chem., 13, 538 (2002)
  25. J. W. Hong, M. Y. Park, H. K. Kim, Y. B. Kim, and H. K. Choi, J. Korean Ind. Eng. Chem., 11, 693 (2000)
  26. J. W. Hong and H. W. Lee, J. Korean Ind. Eng. Chem., 5, 857 (1994)
  27. D. K. Kim, J. K. Lim, and W. G. Kim, J. Korean Ind. Eng. Chem., 15, 749 (2004)